Process for producing granular hematite particles

A process for producing granular hematite particles which have an average particle diameter of 0.05 to 0.6 μm, a hematite content of not less than 97% by weight, an equilibrium water content of not more than 0.5%, a heat resistance of not less than 450° C., a tinting strength of not less than 105%, and a hue having an L* value of 22 to 33, an a* value of 24 to 37 and a b* value of 13 to 40, comprising:

• passing an oxygen-containing gas through an aqueous ferrous nitrate solution in the presence of iron materials and hematite seed crystals at a temperature of 80 to 90° C., thereby obtaining reddish brown precipitates containing granular hematite particles as a main component;
• subjecting the reddish brown precipitates to filtration, water-washing and then drying;
• and
• heat-treating the reddish brown precipitates in air at a temperature of 450 to 900° C.

A process for producing granular hematite particles which have an average particle diameter of 0.4 to 0.6 μm, a hematite content of not less than 98% by weight, an equilibrium water content of not more than 0.25%, a heat resistance of 500 to 800° C., a tinting strength of 105 to 120%, and a hue having an L* value of 22 to 24, an a* value of 24 to 29 and a b* value of 13 to 20, comprising:

• passing an oxygen-containing gas through an aqueous ferrous nitrate solution in the presence of iron materials and hematite seed crystals at a temperature of 80 to 90° C., thereby obtaining reddish brown precipitates containing granular hematite particles as a main component;
• subjecting the reddish brown precipitates to filtration, water-washing and then drying;
• and
• heat-treating the reddish brown precipitates in air at a temperature of 450 to 900° C.

A process for producing granular hematite particles, comprising:

• passing an oxygen-containing gas through an aqueous ferrous nitrate solution at a temperature of 80 to 90° C. in the presence of iron materials and hematite seed crystals obtained by adding dilute nitric acid to an aqueous solution containing the iron materials while maintaining the aqueous solution at a temperature of 90 to 95° C. to form ferric nitrate precipitates and then hydrolyzing the ferric nitrate precipitates at a temperature of 90 to 95° C. for 1 to 4 hours, in an amount of 5 to 40% by weight based on the weight of the granular hematite particles produced, thereby obtaining reddish brown precipitates containing granular hematite particles as a main component;
• subjecting the reddish brown precipitates to filtration, water-washing and then drying;
• and
• heat-treating the reddish brown precipitates in air at a temperature of 450 to 900° C. for 30 to 150 minutes.