Process for producing alkenyl aromatic foams having increased thermal insulation using cycloalkane blowing agent and foams produced thereby
AssigneeReedy International Corporation
InventorsWalter R. Harfmann, Michael E. Reedy
Life of this patent
Estimating the term…
Abstract
Processes for producing alkenyl aromatic foams utilizing a cycloaliphatic gas as blowing agent, are described. Also disclosed are alkenyl aromatic foams produced by the process which exhibit increased thermal insulation properties.
Claims8
A process for the production of alkenyl aromatic foams, said process comprising:
- (a) heating alkenyl aromatic resin to a temperature above its melting point to form a melted alkenyl aromatic resin;
- (b) adding talc to the melted alkenyl aromatic resin to form an alkenyl aromatic/talc blend;
- (c) adding to the alkenyl aromatic/talc blend a non-solid blowing agent comprised of cycloaliphatic gas, wherein said cycloaliphatic gas is present in an amount equal to or greater than the amount of atmospheric gas to form an added melted blend;
- (d) mixing the added melted blend to form a mixed added melted blend;
- and
- (e) extruding and cooling the mixed added melted blend.
An alkenyl aromatic foam comprised of:
- (a) alkenyl aromatic polymer;
- and
- (b) talc, wherein the foam is comprised of closed cells containing cycloaliphatic gas, wherein said cycloaliphatic gas is present in an amount equal to or greater than the amount of atmospheric gas.
An alkenyl aromatic foam comprised of:
- (a) alkenyl aromatic polymer;
- (b) styrene resin;
- (c) rubbery block copolymer;
- and
- (d) the decomposition products of solid blowing agent, wherein the foam is comprised of closed cells containing cycloaliphatic gas, wherein said cycloaliphatic gas is present in an amount equal to or greater than the amount of atmospheric gas.
An alkenyl aromatic foam comprised of:
- (a) alkenyl aromatic polymer;
- (b) styrene resin;
- (c) rubbery block copolymer;
- (d) the decomposition products of solid blowing agent;
- and
- (e) talc, wherein the foam is comprised of closed cells containing cycloaliphatic gas, wherein said cycloaliphatic gas is present in an amount equal to or greater than the amount of atmospheric gas.
A process for the production of alkenyl aromatic foams, said process comprising:
- (a) heating alkenyl aromatic resin to a temperature above its melting point to form a melted alkenyl aromatic resin;
- (b) adding talc to the melted alkenyl aromatic resin to form an alkenyl aromatic/talc blend;
- (c) adding to the alkenyl aromatic talc blend a non-solid blowing agent consisting essentially of cycloaliphatic gas to form an added melted blend;
- (d) mixing the added melted blend to form a mixed added melted blend;
- and
- (e) extruding and cooling the mixed added melted blend.
An alkenyl aromatic foam composition comprised of:
- (a) alkenyl aromatic polymer;
- and
- (b) talc, wherein the foam is comprised of closed cells containing gas consisting essentially of cycloaliphatic gas.
An alkenyl aromatic foam comprised of:
- (a) alkenyl aromatic polymer;
- (b) styrene resin;
- (c) rubbery block copolymer;
- and
- (d) the decomposition products of solid blowing agent, wherein the foam is comprised of closed cells containing gas consisting essentially of cycloaliphatic gas.
An alkenyl aromatic foam comprised of:
- (a) alkenyl aromatic polymer;
- (b) styrene resin;
- (c) rubbery block copolymer;
- (d) the decomposition products of solid blowing agent;
- and
- (e) talc, wherein the foam is comprised of closed cells containing gas consisting essentially of cycloaliphatic gas.