Molding sand appropriate for the fabrication of cores and molds
AssigneeIberia Ashland Chemical, S.A.
InventorJaime Prat Urreiztieta
Life of this patent
Estimating the term…
Abstract
The molding sand comprises hollow microspheres of aluminum silicate, preferably with an aluminum content between 15 and 45% by weight, a wall thickness between 3 and 10% of the particle diameter and a particle size between 10 and 350 μm. These sands are useful to manufacture low density cores with good “veining” and penetration characteristics, moreover maintaining the mechanical properties of the core obtained. These cores are useful in the manufacture of iron casting.
Claims10
A composition for the manufacture of cores and chill molds which comprises a molding sand, a resin and hollow microspheres of aluminum silicate, said hollow microspheres of aluminum silicate being present in the composition in an amount between 1 and 30% by weight of the total amount of the composition and having an aluminum content between 15 and 45% by weight of the microspheres to absorb expansion when the core or chill mold is heated by a molten casting metal and thereby to prevent formation of fissures in the core or chill mold and veining of a cast article.
A method of producing an iron casting comprising:
- introducing a molding sand into a forming mold, said molding sand having a composition comprising:
- sand, a resin and hollow microspheres of aluminum silicate, said hollow microspheres of aluminum silicate being present in the composition in an amount between 1 and 30% by weight of the total amount of the composition and having an aluminum content between 15 and 45% by weight of the microspheres,
- forming a non-cured core or mold in said composition,
- contacting said non-cured core or mold with a gaseous curing catalyst until said core or mold may be handled,
- inserting the core or mold in a casting device,
- pouring an iron casting composition in a liquid state, in said casting device;
- allowing the iron casting composition poured into the casting device to cool and solidify;
- and
- removing the thus solidified iron casting from the casting device,
- said iron casting being free of surface defects including veining due to smoothness of the core or mold as a result of absorption of expansion by said microspheres when the core or mold is heated by the casting metal,
- whereby the iron casting is the target product as is without need for machining.
A method of reducing surface defects including veining in the surface of an iron casting produced by a method comprising:
- introducing a molding composition into a forming mold,
- forming a non-cured core or mold of said composition,
- contacting said non-cured core or mold with a gaseous curing catalyst until said core or mold may be handled,
- inserting the core or mold in a casting device,
- pouring an iron casting composition in a liquid state, into said casting device;
- allowing the iron casting composition poured into the casting device to cool and solidify;
- and
- removing the thus solidified iron casting from the casting device,
- said iron casting being free of surface defects including veining by forming said molding composition as follows:
- sand, a resin and hollow microspheres of aluminum silicate, said hollow microspheres of aluminum silicate being present in the molding composition in an amount between 1 and 30% by weight of the total amount of the molding composition and having an aluminum content between 15 and 45% by weight of the microspheres the presence of said microspheres in the molding composition as aforesaid producing a smoothness of the core or mold as a result of absorption of expansion by said microspheres when the core or mold is heated by the casting metal, whereby the iron casting is obtained as the target product, as is, without need for machining.