Kaolin clay glossing pigment and preparation thereof
AssigneeEngelhard Corporation
InventorsRichard R. Berube, Michael G. Londo, Sathanjheri A. Ravishankar
Life of this patent
Estimating the term…
Abstract
Novel nanosized kaolin clay particles are prepared by agitating a fine particle size fraction of kaolin clay in a Netzsch mill until the particle size is reduced, aspect ratio is decreased and surface area is increased. The ultrafine kaolin particles are especially useful as a pigment to provide high surface gloss to ink jet printing papers.
Claims14
A kaolin clay glossing pigment useful for coating paper comprising individual nanosized particles of kaolin clay having an average aspect ratio below 2.5, the surfaces of said particles of kaolin being substantially free from attached fine particles.
An ultrafine kaolin pigment useful when coated on paper to provide a high gloss surface finish which comprises particles of hydrous kaolin clay that have an average size below 0.2 microns as determined by sedimentation and at least 50% by weight have an aspect ratio of 2.5 or below, a B.E.T. surface area above 25 m2/g, the majority of said particles being further characterized when viewed by scanning electron microscope as being round and substantially free of attached fine particles.
The method for producing an ultra-high glossing pigment from a fine particle size high purity fractionated kaolin clay that is at least 90% by weight finer than 1 micron which comprises:
- (a) forming said fine particle size fractionated clay into a dispersed, fluid aqueous slurry,
- (b) agitating said slurry of clay from step (a) with a particulate grinding media in an agitated disc grinding system that accelerates the grinding media centifugally from the outeredge of the disc, thereby creating shearing forces between the disc and said media, and using kinetic energy imparted to the media by the disc,
- (c) repeating steps (a) and (b) and recovering the resulting smoothed clay particles.