US 6,555,608 B2Granted
White standard paint
AssigneeTopcon Corporation
InventorsTakashi Takahashi, Yukio Ikezawa
Life of this patent
Estimating the term…
Abstract
A standard white paint with good weather resistance and improvement of reflectivity characteristics for UV as well as adhesion to the substrate is provided. The white standard paint of the present invention contains barium sulfate, binder and solvent in which Polyvinyl alcohol is used as binder. The polymerization degree of the polyvinyl alcohol is ranging from 900 to 1100 and the saponification degree is ranging from 86 mol % to 90 mol %.
Claims4
A white standard paint comprising:
- barium sulfate;
- a binder;
- and
- a solvent,
- polyvinyl alcohol being used as ingredient of said binder,
- said polyvinyl alcohol having a polymerization degree ranging from 900 to 1100 and a saponification degree ranging from 86 mol % to 90 mol %, wherein said barium sulfate has a purity degree of 99.9% or more.
3 more elements
A white standard paint comprising:
- barium sulfate;
- and
- a binder;
- polyvinyl alcohol being used as ingredient of said binder,
- said polyvinyl alcohol having a polymerization degree ranging from 900 to 1100 and a saponification degree ranging from 86 mol % to 90 mol %, and a mixture ratio of said barium sulfate and binder being ranging from 0.5 wt. % to 6 wt. %.
2 more elements
A white standard paint comprising:
- barium sulfate;
- a binder;
- a solvent;
- and
- distilled water,
- polyvinyl alcohol being used as ingredient of said binder,
- said solvent being ethanol,
- said barium sulfate having a purity degree of 99.9% or more,
- said polyvinyl alcohol having a polymerization degree ranging from 900 to 1100 and a saponification degree ranging from 86 mol % to 90 mol %, and
- a mixture of said barium sulfate, polyvinyl alcohol, ethanol, and distilled water having ratios in which the barium sulfate is 43.3 wt. %, the polyvinyl alcohol is 2.7 wt % the ethanol is 27.0 wt. % and the distilled water is residual.
7 more elements
A white standard paint comprising:
- barium sulfate;
- a binder;
- a solvent;
- and
- distilled water,
- polyvinyl alcohol being used as ingredient of said binder, said solvent being ethanol,
- said polyvinyl alcohol having a polymerization degree ranging from 900 to 1100 and a saponification degree ranging from 86 mol % to 90 mol %, and
- said barium sulfate having a purity degree of 99.9% or more, and a mixture of said barium sulfate, polyvinyl alcohol, ethanol, and distilled water having mixture ratios in which the barium sulfate is 44.7 wt. %, the polyvinyl alcohol is 1.3 wt % the ethanol is 27.0 wt. % and the distilled water is residual.
5 more elements
Dependencies are inferred from the claim text.