Abstract

A process is disclosed for obtaining colloid-forming metal particles from an aqueous mine waste solution containing that metal in ionic form. In accordance with this process, an aqueous mine waste solution containing that metal in ionic form is provided having a pH value of about 4.0 to about 6.5. The solution is electrified with direct current a about 1.2 to about 2.0 volts to reduce the desired metal ions to colloidal metal particles. A slurry of cellulose particles is agitatingly added to the colloid composition followed by a flocculant to form a solid phase cellulosic floc containing the colloid. The solid and liquid phases are separated, and the solid phase is dried, fluxed and heated to a temperature sufficient to melt the flux and colloid and form larger metal particles that can then be recovered. The colloid-forming metal is preferably gold.

Claims20

Dependent claims

A process for obtaining a desired colloid-forming metal from a solution containing that metal in ionic form that comprises the steps of:

(a) providing an aqueous mine waste water solution containing a desired colloid-forming metal in ionic form having a pH value of about 4.0 to about 6.5;
(b) passing direct current at about 1.2 to about 2 volts through the solution for a time period sufficient to convert the desired metal ions into colloidal metal and form a colloidal metal-containing composition;
(c) agitatingly admixing cellulose particles with the colloidal metal-containing composition to form an agitated slurry of cellulose particles admixed with the colloidal metal;
(d) admixing a flocculating agent with the agitated slurry to form a settling composition containing a cellulosic floc;
(e) maintaining the settling composition in the absence of agitation for a time period sufficient to form two phases, a first phase that contains water and a solid phase comprising colloidal metal entrapped within a cellulosic floc and a second liquid discharge water phase having a reduced concentration of desired metal;
(f) separating the solid and liquid phases;
(g) drying the solid phase;
and
(h) fluxing the solid phase and heating the fluxed solid phase to a temperature sufficient to melt the colloidal metal present to form larger particles of the desired metal and to burn off the cellulosic floc.

6 more elements

A process for obtaining a desired colloid-forming metal from a solution containing that metal in ionic form that comprises the steps of:

(a) providing an aqueous mine waste water solution containing a desired colloid-forming metal in ionic form present in a concentration of about 0.005 to about 1.5 milligrams per liter and having a pH value of about 4.0 to about 5.0;
(b) passing direct current at about 1.2 to about 1.8 volts through the solution for a time period sufficient to convert the desired metal ions into colloidal metal and form a colloidal metal-containing composition;
(c) agitatingly admixing cellulose particles of waste news papers that have been macerated in water to form a pulp with the colloidal metal-containing composition to form an agitated slurry of cellulose particles admixed with the colloidal metal;
(d) admixing a flocculating agent with the agitated slurry to form a settling composition containing a cellulosic floc;
(e) maintaining the settling composition in the absence of agitation for a time period sufficient to form two phases, a first phase that contains water and a solid phase comprising colloidal metal entrapped within a cellulosic floc and a second liquid discharge water phase having a reduced concentration of desired metal;
(f) separating the solid and liquid phases by filtration or centrifugation;
(g) drying the solid phase;
(h) fluxing the solid phase and heating the fluxed solid phase to a temperature sufficient to melt the colloidal metal present to form larger particles of the desired metal and to burn off the cellulosic floc;
and
(i) collecting the larger particles of the desired metal.

7 more elements

A process for obtaining a desired colloid-forming metal from a solution containing that metal in ionic form that comprises the steps of:

(a) providing an aqueous mine waste water solution containing a desired colloid-forming metal in ionic form present in a concentration of about 0.005 to about 1.5 milligrams per liter and having a pH value of about 4.0 to about 5.0, said desired metal being selected from the group consisting of gold, silver and the platinum group of metals;
(b) passing direct current at about 1.2 to about 1.8 volts through the solution for a time period sufficient to convert the desired metal ions into colloidal metal and form a colloidal metal-containing composition;
(c) agitatingly admixing cellulose particles of waste news papers that have been macerated in water to form a pulp with the colloidal metal-containing composition to form an agitated slurry of cellulose particles admixed with the colloidal metal;
(d) admixing guar gum as a flocculating agent with the agitated slurry to form a settling composition containing a cellulosic floc;
(e) maintaining the settling composition in the absence of agitation for a time period sufficient to form two phases, a first phase that contains water and a solid phase comprising colloidal metal entrapped within a cellulosic floc and a second liquid discharge water phase having a reduced concentration of desired metal;
(f) separating the solid and liquid phases by filtration;
(g) drying the solid phase;
(h) fluxing the solid phase and heating the fluxed solid phase at two temperatures, wherein said fluxed solid phase is first heated at a lower temperature sufficient to char the cellulosic floc and then heated at a higher temperature sufficient to melt the flux and colloidal metal present to form larger particles and to burn off the cellulosic floc;
(i) collecting the larger particles of the desired metal;
and
(j) returning the separated discharge water to the source from which said aqueous mine waste water solution was obtained at a down stream position.

8 more elements

Dependencies are inferred from the claim text.