Dry paint transfer process and product

A dry paint transfer process for making a plastic vehicular body panel having an exterior automotive quality paint coat on a contoured outer surface of the body panel, in which the paint coat on the body panel has a glossy clear coat/color coat paint finish, the process comprising:

• (a) coating an optically clear weatherable and hardenable thermoplastic and thermoformable polymeric clear coat material onto a smooth high gloss surface of a carrier comprising a flexible high-temperature-resistant polymeric casting sheet, the clear coat material comprising an alloy of polyvinylidene fluoride (PVDF) and an acrylic resin which contains from about 50% to about 70% PVDF and from about 30% to about 50% acrylic resin, by weight of the total PVDF and acrylic resin solids present in the clear coat;
• (b) hardening the liquid polymeric material to form a thermoplastic and thermoformable optically clear film having a first, exposed face and a second face contiguous with the smooth surface of the carrier;
• (c) applying to the first, exposed face of the clear film a pigmented color coat comprising a thermoplastic and thermoformable polymeric material with pigments distributed therein, and hardening the color coat to form a clear coat/color coat paint film supported by the carrier;
• (d) applying an adhesive layer to the color coat side of the clear coat/color coat paint film;
• (e) transferring the clear coat/color coat paint film from the carrier to a preformed continuous and self-supporting semi-rigid thermoformable polymeric backing sheet having a thickness from about 10 to about 40 mils, by the steps of supporting the clear coat/color coat paint film on the carrier while joining the carrier-supported clear coat/color coat paint film with the backing sheet under the application of heat and pressure for adhering the adhesive layer to the backing sheet to bond the clear coat/color coat paint film to the backing sheet, and separating the carrier from the composite of the backing sheet and the clear coat/color coat paint film to expose the second face of the clear coat as a glossy, smooth outer surface, the clear coat/color coat paint film having an elongated state in which the film is sufficiently pliable under the application of heat and pressure during thermoforming to stretch the clear coat/color coat paint film when conforming the film to a contoured shape;
• (f) thermoforming the composite of the backing sheet and the clear coat/color coat paint film to thermoplastically form a three-dimensionally shaped paint-coated laminate which retains its contoured shape upon thermoforming and in which regions of the clear coat/color coat paint film are subjected to said elongated state while the paint film on the laminate retains said glossy, smooth outer surface, the paint film on said laminate having a gloss level of at least 75 gloss units measured at 60° following said thermoforming step, the laminate thereby providing the outer component of a vehicular body panel having a contoured outer surface with a clear coat/color coat paint film of exterior automotive quality;
• and
• (g) placing the shaped laminate in a mold with the backing sheet thereof facing away from a contoured mold surface of the mold, the laminate having been thermoformed to a shape conforming to the shape of the contoured mold surface, and molding a resinous substrate material to the backing sheet to form a molded contoured vehicular body panel in which the paint-coated laminate forms a decorative clear coat/color coat paint finish bonded to the outer surface of the molded body panel with the pigmented color coat layer visible through the outer clear coat, the backing sheet having sufficient thickness to absorb defects present in the resinous substrate material to produce an essentially defect-free outer surface with a retained 60° gloss value of at least 75 on the finished body panel.

A dry paint transfer process for making a plastic vehicular body panel having an exterior automotive quality paint coat on a contoured outer surface of the body panel, in which the paint coat on the body part has a glossy clear coat/color coat paint finish, the process comprising:

• (a) coating an optically clear weatherable and hardenable thermoplastic and thermoformable polymeric clear coat material onto a smooth high gloss surface of a carrier comprising a flexible high-temperature-resistant polymeric casting sheet having a heat resistance greater than about 450° F., the clear coat material comprising an alloy of polyvinylidene fluoride (PVDF) and an acrylic resin which contains from about 50% to about 70% PVDF and from about 30% to about 50% acrylic resin, by weight of the total PVDF and acrylic resin solids present in the clear coat;
• (b) hardening the liquid polymeric material to form a thermoplastic and thermoformable optically clear film having a dry film thickness from about 0.5 mil to about 1.5 mil, and having a first, exposed face and a second face contiguous with the smooth surface of the carrier;
• (c) applying to the first, exposed face of the clear film a pigmented color coat comprising a thermoplastic and thermoformable polymeric material with pigments distributed therein, and hardening the color coat to form a clear coat/color coat paint film supported by the carrier, the color coat having a dry film thickness from about 0.5 mil to about 1.5 mil;
• (d) applying an adhesive layer to the color coat side of the clear coat/color coat paint film;
• (e) transferring the clear coat/color coat paint film from the carrier to a preformed continuous and self-supporting semi-rigid thermoformable polymeric backing sheet having a thickness from about 10 to about 40 mils, by the steps of supporting the clear coat/color coat paint film on the carrier while joining the carrier-supported clear coat/color coat paint film with the backing sheet under the application of heat and pressure for adhering the adhesive layer to the backing sheet to bond the clear coat/color coat paint film to the backing sheet, and separating the carrier from the composite of the backing sheet and the clear coat/color coat paint film to expose the second face of the clear coat as a glossy, smooth outer surface, the clear coat/color coat paint film having an elongated state in which the film is sufficiently pliable under the application of heat and pressure during thermoforming to stretch the clear coat/color coat paint film when conforming the film to a contoured shape;
• (f) thermoforming the composite of the backing sheet and the clear coat/color coat paint film by subjecting the composite to heat from about 270° to about 450° F. and vacuum pressure to thermoplastically form a three-dimensionally preshaped paint-coated laminate which retains its contoured shape upon thermoforming and in which regions of the clear coat/color coat paint film are subjected to elongation greater than 40% while the paint film on the laminate retains said glossy, smooth outer surface, the paint film on said laminate having a gloss level of at least 75 gloss units measured at 60° following said thermoforming step, the laminate thereby providing the outer component of a vehicular body part having a contoured outer surface with a clear coat/color coat paint film of exterior automotive quality;
• and
• (g) placing the shaped laminate in a mold with the backing sheet thereof facing away from a contoured mold surface of the mold, the laminate having been thermoformed to a shape conforming to the shape of the contoured mold surface, and molding a resinous substrate material to the backing sheet to form a molded contoured vehicular body panel in which the paint-coated laminate forms a decorative clear coat/color coat paint finish bonded to the outer surface of the molded body panel with the pigmented color coat layer visible through the outer clear coat, the backing sheet having sufficient thickness to absorb defects present in the resinous substrate material to produce an essentially defect-free outer surface with a retained 60° gloss value of at least 75 on the finished body panel.