Composition useful for making in-situ silicon carbide whiskers and fibres

Abstract

A composition useful for making in-situ silicon carbide whiskers and fibers in an inorganic composite matrix selected from silicon carbide carbon and carbon composite matrix, wherein the said composition comprises: Natural Fiber (1.6-6.5 Wt %); TetraEthyl Orthosilicate (10.4-42 Wt %); Phenolic Resin (38-73.5 Wt %); Curing agent (4.2-11 Wt %); Optionally, Silicon Carbide (9.4-12 Wt %); Organic Solvent (requisite amount to dissolve the Phenolic resin). The fiber preferably is a natural fiber selected from the group consisting of jute, sisal, hem and other natural fiber having cellulosic or hemicellulosic constituent at its backbone. The curing agent preferably is selected from hexamine, para toluenesulphonic acid and para formaldehyde, most preferably hexamine. The molecular weight of phenolic resin preferably is in the range of 450-700, and the organic solvent preferably is selected from methanol, toluene and benzene.