Method for manufacturing a radiation shielding material
AssigneeArntz Beteiligungs GmbH & Co. KG
InventorWolfgang Lange
Life of this patent
Estimating the term…
Abstract
A radiation shielding material is manufactured from an elastomer that is blended with a radiation-absorbing filler material. The filler material comprises a powder of a metal with a high atomic member, or compounds thereof. The filler material is represented by more than 80 percent weight and has a grain size distribution in the range of 20 μm to 120 μm. The filler material is mixed with a loading material in powdered form. That mixture is kneaded with the elastomer within a mixer while the temperature is maintained below 180° C. The kneaded mixture is cooled and then cut into strips. The strips are passed through a strainer having a mesh width of between 5 μm and 1000 μm. The strained strips are then formed into a foil.
Claims20
Method for manufacturing a radiation shielding material from a polymer that is blended with a radiation-absorbing filler material, the polymer being an elastomer comprising a synthetic thermoplastic, vulcanizable elastomer, or a non-vulcanizing elastomer;
- wherein the vulcanizable elastomer is natural rubber (NR), polychloroprene (CR), nitrile-butadiene (NBR), styrene-butadiene rubber (SBR), butadiene rubber (BR), ethylene propylene terpolymer (EPM), ethylene propylene copolymer (EPM), polyurethane (PU), isobutylene-isoprene rubber, silicone rubber (VMO and MQ), ethylene vinyl acetate rubber (EVA) or blends thereof, wherein the non-vulcanizing elastomer is polypropylene/EPDM (PP/EPDM), styrene-ethylene-butylene-styrene (SEBS), polyvinyl-chloride-nitrile-butadiene (NBR/PVC), ethylene propylene copolymer (EPM), or blends thereof;
- the radiation absorbing filler material comprising a powder of an element with a high atomic number or compounds thereof selected from the group consisting of antimony, barium, bismuth, bromine, cadmium, cerium, cesium, gold, iodine, indium, iridium, lead, mercury, molybdenum, osminium, platinum, polonium, rhenium, rhodium, silver, strontium, tantalum, thorium, tin, tungsten, uranium, zirconium, elements from the lanthanide group and elements from the actinide group, represented by more than 80 weight percent, and having a grain size distribution in the range of 20 μm to 120 μm, the method including the steps of:
- A) mixing with the filler material a loading material in powdered form so as to improve wettability of the filler material with respect to the elastomer;
- the loading material comprising magnesium aluminum silicate, zinc stearate, silicone resin powder, strontium carbonate, barium carbonate, barium sulfate, calcium tungstate, gadolinium oxi-sulfide, barium sulfate doped with tin dioxide, zinc, antimony, elements from the lanthanide series or elements from the actinide series or mixtures thereof, wherein the loading material is a material that is different from the filler material;
- B) kneading the mixture of step A together with the elastomer inside a mixer while maintaining a temperature thereof below 180° C.;
- C) removing the kneaded mixture from the mixer and passing the kneaded mixture through cooled roll mills wherein the kneaded mixture is cooled and homogenized;
- D) cutting the cooled and homogenized mixture into strips on a strip cutting apparatus;
- E) passing the strips through a strainer having a mesh width of between 5 μm and 1000 μm;
- and
- F) forming the strained mixture into a foil.
Method for manufacturing a radiation shielding material from a polymer that is blended with a radiation-absorbing filler material, the polymer being an elastomer selected from the group consisting of a synthetic thermoplastic, vulcanizable elastomer, and a non-vulcanizing elastomer;
- the vulcanizable elastomer selected from the group consisting of natural rubber (NR), polychloroprene (CR), nitrile-butadiene (NBR), styrene-butadiene rubber (SBR), butadiene rubber (BR), ethylene propylene terpolymer (EPM), ethylene propylene copolymer (EPM), polyurethane (PU), isobutylene-isoprene rubber, silicone rubber (VMO and MQ), ethylene vinyl acetate rubber (EVA) and blends thereof;
- the non-vulcanizing elastomer selected from the group consisting of polypropylene/EPDM (PP/EPDM), styrene-ethylene-butylene-styrene (SEBS), polyvinyl-chloride-nitrile-butadiene (NBR/PVC), ethylene propylene copolymer (EPM), and blends thereof;
- the radiation absorbing filler material comprising a powder of an element with a high atomic number or compounds thereof selected from the group consisting of antimony, barium, bismuth, bromine, cadmium, cerium, cesium, gold, iodine, indium, iridium, lead, mercury, molybdenum, osminium, platinum, polonium, rhenium, rhodium, silver, strontium, tantalum, thorium, tin, tungsten, uranium, zirconium, elements from the lanthanide group and elements from the actinide group, represented by more than 80 weight percent, and having a grain size distribution in the range of 20 μm to 120 μm, the method including the steps of:
- A) mixing with the filler material a loading material in powdered form so as to improve wettability of the filler material with respect to the elastomer;
- the loading material selected from the group consisting of magnesium aluminum silicate, zinc stearate, silicone resin powder, strontium carbonate, barium carbonate, barium sulfate, calcium tungstate, gadolinium oxi-sulfide, barium sulfate doped with tin dioxide, zinc, antimony, elements from the lanthanide series and elements from the actinide series and mixtures thereof, wherein the loading material is a material that is different from the filler material;
- B) kneading the mixture of step A together with the elastomer inside a mixer while maintaining a temperature thereof below 180° C.;
- C) removing the kneaded mixture from the mixer and passing the kneaded mixture through cooled roll mills wherein the kneaded mixture is cooled and homogenized;
- D) cutting the cooled and homogenized mixture into strips on a strip cutting apparatus;
- E) passing the strips through a strainer having a mesh width of between 5 μm and 1000 μm;
- and
- F) forming the strained mixture into a foil.
Dependencies are inferred from the claim text.