Carpet material and method of producing same

A floor carpet for an automotive vehicle, formed of a carpet material, said carpet material comprising:

• a base fabric layer for supporting a pile layer, formed of nonwoven fabric and integral with said pile layer;
• and
• a backing layer located at an opposite side of said base fabric layer with respect to said pile layer, said backing layer being formed of nonwoven fabric and integral with said base fabric layer, said nonwoven fabric forming said backing layer including polyester-based staple fiber in an amount ranging from 80 to 20% by weight, and binder fiber in an amount ranging from 20 to 80% by weight, said binder fiber being of a core and sheath type conjugate structure and having a core formed of high melting point polyester, and a sheath formed of low melting point copolyester, said nonwoven fabric forming said backing layer having a storage elastic modulus in a dynamic viscoelasticity test, ranging from 5 to 10 Pa within a measuring temperature range of from 0 to 50° C.;
• wherein said nonwoven fabric forming said backing layer has a surface density ranging from 100 to 1000 g/m2 and 1.5 to 5 times that of the nonwoven fabric forming said pile layer and is formed of polyester-based fiber having a diameter ranging from 20 to 130 μm, said base fabric layer and said backing layer being formed integral with each other by a needle punch treatment, said needle punch treatment by a needle punch device being made in a direction of from said backing layer to said base fabric layer, so as to push out a part of said base fabric layer to form said pile layer.

A floor carpet for an automotive vehicle, said floor carpet being formed of a carpet material, said carpet material comprising:

• a base fabric layer for supporting a pile layer, formed of nonwoven fabric and integral with said pile layer, said nonwoven fabric being formed of polyester-based fiber;
• and
• a backing layer located at an opposite side of said base fabric layer with respect to said pile layer, said backing layer being formed of nonwoven fabric and integral with said base fabric layer, said nonwoven fabric being formed of polyester-based fiber;
• wherein said backing layer has a thickness ranging from 10 to 50% relative to a whole thickness of said carpet material, and a storage elastic modulus (log E′) in a dynamic viscoelasticity test, ranging from 5 to 10 Pa within a measuring temperature range of from 0 to 50° C.;
• wherein said nonwoven fabric forming said backing layer has a surface density ranging from 100 to 1000 g/m2 and 1.5 to 5 times that of the nonwoven fabric forming said pile layer and is formed of polyester-based fiber having a diameter ranging from 20 to 130 μm;
• wherein said nonwoven fabric forming said backing layer is formed of a mixture of polyester-based staple fiber having a diameter ranging from 20 to 130 μm, and binder fiber in an amount ranging from 20 to 80% by weight, said binder fiber being of a core and sheath conjugate structure and having a core formed of polyester, and a sheath formed of low melting point copolyester having a melting point ranging from 110 to 180° C.;
• wherein said base fabric layer and said backing layer are formed integral with each other by a needle punch treatment, said needle punch treatment by a needle punch device being made in a direction of from said backing layer to said base fabric layer, so as to push out a part of said base fabric layer to form said pile layer.