Abstract
The invention is directed toward a sterile bone structure for application to a bone defect site to promote new bone growth at the site comprising a partially demineralized cortical bone structure, said bone structure comprising a cross sectional surface are ranging from 85% to 95% of the original bone surface area before demineralization with the remaining partially demineralized cortical bone structure having an outer demineralized layer ranging in thickness from about 0.05 mm to about 0.14 mm and a mineralized core.
Claims19
A method for partially demineralizing a previously shaped cortical bone structure comprising the steps of:
- a) soaking said previously shaped cortical bone structure in an acid solution for a time period at a temperature less than about 30° C. to remove a layer of the cortical bone structure and produce a demineralized layer on the cortical bone structure ranging from about 0.05 mm to about 0.08 mm with the remaining area comprising mineralized bone, the cortical bone structure after partial demineralization being rigid and maintaining substantially its original mechanical strength;
- b) agitating the acid solution and immersed cortical bone structure;
- c) removing the cortical bone structure from the acid solution and washing the cortical bone structure until the wash discard is at about a neutral pH;
- d) packaging the cortical bone structure in a moisture permeable container;
- and
- e) lyophiizig the cortical bone structure.
3 more elements
A method for partially dernineralizing a previously shaped hone structure comprising the steps of:
- a) soaking said previously shaped cortical bone structure having a thickness greater than 1.5 mm in an acid solution for 30 to 90 minutes at ambient temperature to remove a layer of the cortical bone structure ranging from 0.12 mm to 0.40 mm of the surface area and produce bone structure with a mineralized center section and a demineralized layer around said mineralized center section ranging in thickness from about 0.08 mm to about 0.14 mm bone, the cortical bone structure after demineralization being rigid;
- b) simultaneously agitating the acid solution and immersed cortical bone structure by stirring same;
- c) removing the partially demineralized cortical bone structure from the acid solution and washing the cortical bone structure with sterile pure water until the wash discard is at about a neutral pH;
- d) lyophilizing the cortical bone structure;
- and
- e) packaging the cortical bone structure in a moisture permeable container.
3 more elements
A method for partially demineralizing a previously shaped bone structure comprising the steps of:
- a) soaking a formed cortical bone structure in an aqueous antibiotic solution;
- b) placing the soaked cortical bone structure in an aqueous detergent at about 95 degrees F;
- c) applying ultrasonic energy to enhance penetration of said detergent;
- d) washing the shaped cortical bone structure for at least 60 minutes in an alcohol/water solution;
- e) soaking a formed cortical bone structure in an acid solution for 15 to 30 minutes to remove a layer of the cortical bone structure and produce a demineralized layer ranging from about 0.05 mm to 0.08 mm in thickness bone, the cortical bone structure after deminerazzation being rigid;
- f) agitating the acid solution with said immersed cortical bone structure;
- g) removing the cortical bone structure from the acid solution and washing the cortical bone structure until the wash discard is at about a neutral pH;
- h) lyophilizing the cortical bone structure;
- and
- i) packaging the cortical bone structure in a moisture permeable container.
7 more elements
A method for partially demineralizing a previously shaped bone structure comprising the steps of:
- a) soaking a formed cortical bone structure in an aqueous antibiotic solution;
- b) placing the soaked cortical bone structure in an aqueous detergent at about 95 degrees F;
- c) applying ultrasonic energy to enhance penetration of said detergent;
- d) washing the shaped cortical bone structure for at least 60 minutes in an alcohol/water solution;
- e) soaking a formed cortical bone structure in an acid solution for 15 to 30 minutes to remove a layer of the cortical bone structure and produce a demineralized layer ranging from about 0.05 mm to 0.08 mm in thickness bone, the cortical bone structure after demineralization being rigid;
- f) agitating the acid solution with an immersed cortical bone structure;
- g) removing the cortical bone structure from the acid solution and washing the cortical bone structure until the wash discard is at about a neutral pH;
- h) adding a soluble silver compound to the demineralized layer;
- i) lyophilizing the cortical bone structure;
- and
- j) packaging the cortical bone structure in a moisture permeable container.
8 more elements
A method for partially dernineralizing a previously shaped cortical bone structure comprising the steps of:
- a) soaking said previously shaped cortical bone structure in an acid solution for a time period at a temperature less than about 30° C. to remove a layer of the cortical bone structure while maintaining a cross sectional area of the cortical bone structure ranging from about 85% to about 95% and produce a demineralized layer on the cortical bone structure ranging from about 0.05 mm to about 0.08 mm with the remaining area comprising mineralized bone, the cortical bone structure after partial demineralization being rigid and maintaining suitable compression and bending strength;
- b) agitating the acid solution and immersed cortical bone structure;
- c) removing the cortical bone structure from the acid solution and washing the cortical bone structure until the wash discard is at about a neutral pH;
- d) packaging the cortical bone structure in a moisture permeable container;
- and
- e) lyophilizing the cortical bone structure.
3 more elements
Dependencies are inferred from the claim text.