Process for the manufacture of components on glass substrates that have to be sealed, such as flat display screens of the plasma-panel type
AssigneeThomson Licensing S. A.
InventorGuy Baret
Life of this patent
Estimating the term…
Abstract
The process for manufacturing a plasma display panel, wherein two glass substrates are sealed together using a sealing material of epoxy or polyvinyl butyrate. The sealed structure provides a space between the substrates to contain a discharge gas. The choice of an epoxy or polyvinyl butyrate sealing material allows for relatively low processing temperatures in order to cure the sealing material. This relatively low processing temperature, of between 200° C. and 300° C., lowers the risk of cracking or microcracking of intermediate layers, which are formed on the surfaces of the substrates.
Claims19
A process for producing a plasma display panel having a first and second glass substrate, wherein each substrate comprises a planar surface, and said planar surface of the first substrate is opposed in parallel to said planar surface of the second substrate, said process comprising the steps of:
- depositing a seal on said surface of at least one of the glass substrates wherein the seal is epoxy or polyvinyl butyrate;
- placing the first and second substrates over one another with the seal interposed therebetween to form a seal and a glass substrate assembly;
- curing the seal to fasten the glass substrates to each other and to form a space between the glass substrates within the cured seal;
- vacuum pumping the space;
- filling the space with a discharge gas via a means of access;
- and
- sealing the means of access, wherein the curing step comprises maintaining the seal and glass substrate assembly for about 30 to 60 minutes at a temperature of between 200° to 300° Centigrade.
A process for manufacturing a plasma display panel having a first glass substrate comprising a planar surface having at least one array of first electrodes deposited thereon and a second glass substrate comprising a planar surface having at least one array of second electrodes deposited thereon, wherein said planar surface of the first substrate is opposed in parallel to said planar surface of the second substrate, said process comprising the steps of:
- depositing a layer of organic dielectric material on the planar surface of the first glass substrate and optionally on the planar surface of the second glass substrate, at a temperature sufficient to cure the dielectric layer;
- forming a barrier layer on the dielectric material of the second glass substrate, when present, wherein the barrier layer has a prescribed pattern projecting toward the first glass substrate, at a temperature sufficient to cure the barrier layer;
- depositing a seal on said surface of at least one of the glass substrates, wherein the seal comprises a material layer selected form the group consisting of epoxy and polyvinyl butyrate;
- and
- bonding the glass substrates to each other by curing the seal therebetween, whereby a space is formed between the glass substrates within the cured seal, and wherein said space contains a discharge gas.