Method of fabricating a highly reliable gate oxide

Abstract

An ultra-thin gate oxide layer of hafnium oxide (HfO2) and a method of formation are disclosed. The ultra-thin gate oxide layer of hafnium oxide (HfO2) is formed by a two-step process. A thin hafnium (Hf) film is first formed by thermal evaporation at a low substrate temperature, after which the thin hafnium film is radically oxidized using a krypton/oxygen (Kr/O2) high-density plasma to form the ultra-thin gate oxide layer of hafnium oxide (HfO2). The ultra-thin gate oxide layer of hafnium oxide (HfO2) formed by the method of the present invention is thermally stable in contact with silicon and is resistive to impurity diffusion at the HfO2/silicon interface. The formation of the ultra-thin gate oxide layer of hafnium oxide (HfO2) eliminates the need for a diffusion barrier layer, allows thickness uniformity of the field oxide on the isolation regions and, more importantly, preserves the atomically smooth surface of the silicon substrate.