Method of operating a rotary hearth furnace
AssigneeKabushiki Kaisha Kobe Seiko Sho
InventorsTakao Harada, Masahiko Tetsumoto, Hidetoshi Tanaka
Life of this patent
Estimating the term…
Abstract
To provide an operating method of a rotary hearth furnace for producing reduced iron in which a stuck substance stuck on the hearth surface is removed from the hearth surface to thereby prevent or reduce the wear of the knife edge of a screw of a discharge device, enabling continuous operation for a long period and capable of achieving high availability factor. The hearth surface is quenched by spraying or the like to generate cracks in the stuck substance on the hearth, and the stuck substance is scraped to thereby remove it from the hearth.
Claims17
An operating method of a rotary hearth type reducing furnace for producing reduced metal from raw material comprising at least metal oxide and carbonaceous material, the method including the sequential steps of:
- discharging a reduced metal;
- quenching a hearth surface of said rotary hearth type reducing furnace sufficiently to form a crack in a substance stuck to said hearth surface, and
- removing the stuck substance from said hearth.
An operating method of a rotary hearth type reducing furnace for producing reduced metal from raw material comprising at least metal oxide and carbonaceous material, the method including the sequential steps of:
- discharging a reduced metal;
- applying mechanical shock to a hearth surface, and
- removing the stuck substance from said hearth.
An operating method of a rotary hearth type reducing furnace for heating and reducing raw material comprising at least metal oxide and carbonaceous material to produce reduced metal, the method including the steps of:
- discharging a reduced metal;
- quenching a hearth surface of said rotary hearth type reducing furnace from which the reduced material has been removed, sufficiently to form a crack in a substance stuck to said hearth surface,
- applying mechanical shock to the hearth surface from which the reduced material has been removed, and
- removing the stuck substance from said hearth.
An operating method of a rotary hearth type reducing furnace for heating and reducing raw material comprising at least powdery metal oxide and powdery carbonaceous material to produce reduced metal, wherein a hearth surface of said rotary hearth type reduced furnace, from which the reduced metal has been removed, is quenched to generate a crack in a stuck substance stuck on said hearth, after which said stuck substance is removed from said hearth.
An operation method of a rotary hearth type reducing furnace for heating and reducing raw material comprising at least powdery metal oxide and powdery carbonaceous material to produce reduced metal, wherein mechanical shock is applied to a hearth surface of said rotary hearth type reducing furnace, from which the reduced metal has been removed, to generate a crack in a stuck substance stuck on said hearth, after which said stuck substance is removed from said hearth.
An operating method of a rotary hearth type reducing furnace for heating and reducing raw material comprising at least powdery metal oxide and powdery carbonaceous material to produce reduced metal, wherein a hearth surface of said rotary hearth type reducing furnace, from which the reduced metal has been removed, is quenched to generate a crack in a stuck substance stuck on said hearth, and mechanical shock is applied to said hearth surface, from which the reduced metal has been removed, after which said stuck substance is removed from said hearth.
Dependencies are inferred from the claim text.