Laser consolidation methodology and apparatus for manufacturing precise structures

In a laser process for fabricating components, the steps of:

• (a) providing a substrate;
• (b) supplying material to the substrate at a controlled rate in a direction substantially normal to the substrate;
• (c) providing a conical beam of laser energy arranged around the material supply directed at the area where the material reaches the substrate, the conical beam being at an angle in the range of 25° to 30° to the normal to form a heated annulus around the area;
• (d) controlling the energy and size of the laser beam so that the added material melts and forms together with underlying material a molten zone maintained spherical under the influence of surface tension;
• and
• (e) causing relative movement between the substrate and the material surface and laser beam whereby the supplied material solidifies and forms a uniform ridge with a semi-circular cross section and a linear edge along the substrate.

A method for the deposition of layers of material on a work surface, comprising:

• providing a controlled feed of metallic material normal to the work surface;
• reflecting a laser beam of circular cross-section from divergent faces of a pyramidal mirror to produce a plurality of beams;
• reflecting each of the plurality of beams from spherical mirrors to provide beams at an angle to the material feed between 25° to 30° focused on and substantially surrounding the material arriving at the work surface;
• whereby the material melts and is maintained in a molten spherical configuration by surface tension;
• and
• permitting the molten material to rapidly solidify and form a smooth surfaced uniform ridge of semicircular cross-section.

A method for the deposition of layers of material on a work surface, comprising:

• reflecting a laser beam of circular cross-section from divergent faces of a wedge shaped mirror to produce a pair of beams of semicircular cross-section;
• reflecting each semicircular beam from a spherical mirror so that the two semicircular beams are focused on a substrate, to define a heated circular area;
• whereby the surface of the substrate is melted to form a circular pool, having the same radius as the heated circular area;
• providing a controlled feed of metallic powder normal to the work surface to impact it on the heated circular area;
• whereby a controlled amount of power is injected, melts and increases the level of the molten material above the surface of the substrate to form a spherical configuration by the action of surface tension;
• and
• permitting the molten powder to rapidly solidify, forming a smooth surfaced ridge with a semicircular cross-section.

Apparatus for deposition of layers of material on a work surface, comprising:

• a material feed extending normally to the work surface;
• a laser;
• a prism with divergent reflecting surfaces impacted by the laser beam to provide a plurality of beams;
• and
• a corresponding plurality of concave mirrors each receiving one of the beams and reflecting the beam towards the work surface at an angle to the material feed between 25° to 30° and focusing the beams to form a heated annulus around the area where the material impacts the work surface;
• whereby the material is melted and maintained in molten spherical configuration by surface tension.

Apparatus for deposition of layers of material on a work surface, comprising:

• a material feed extending normally to the work surface;
• a laser;
• a means to diverge the laser beam into a low density expanded laser beam;
• a conical mirror impacted by the laser beam to provide a diverging conical beam and reflecting it as a converging conical beam towards the work surface at an angle to the material feed between 25° to 30° and focusing the beam to form a heated annulus around the area where the material impacts on the work surface;
• whereby the material is melted and maintained in a molten spherical configuration by surface tension.

Apparatus for manufacturing precise structures, comprising:

• a powder feed substantially normal to a work surface;
• a low density laser beam;
• a spherical focusing mirror;
• a conical mirror projecting said laser beam onto said spherical focusing mirror;
• and
• said spherical focusing mirror focusing said beam in a conical pattern at an angle of 25° to 30° to the normal, producing a heated uniform annulus on the work surface, surrounding the area where the powder feed impacts on the surface.