Fluorinating an optical fiber preform in a pure aluminum oxide muffle tube
OwnerFranklin W. Dabbyinventor
Life of this patent
Estimating the term…
Abstract
A method for fabricating fluorine doped, silica based glass and fiber by depositing a layer of high purity silica soot on a core rod while rotating the core rod places the rod of pure fused silica or doped fused silica and silica soot in a furnace having a lining of Al2O3, elevates the temperature in a fluorine rich atmosphere to establish the proper differential in the indices of refraction between the core start rod and the deposited layer, and heats the resulting rod at consolidation temperatures in an atmosphere of helium to form a preform. The apparatus includes a furnace having a lining of high purity alumina that is resistant to chemical etching and change normally due to the fluorine and chlorine.
Claims11
A method of making a fluorine-doped, silica-based glass in a structure having an interior and an interior surface comprising the steps of:
- a. fluorinating silica soot in the interior of the structure the interior surface of the structure being formed of aluminum oxide, and the aluminum oxide having a concentration of at least about 99.97% facing the soot;
- and
- b. forming the silica soot into the glass.
A method of making a fluorine-doped silica-based glass comprising the steps of:
- a. placing a preform of soot into a structure that at least partially encloses the preform, the structure comprising a surface facing the preform of soot, and the surface comprising aluminum oxide having a concentration of at least about 99.97%;
- b. rotating the preform;
- c. heating the interior of the structure to a dissociation temperature;
- d. fluorinating the preform while maintaining the dissociation temperature within the structure;
- and
- e. heating the preform to a consolidation temperature for a time sufficient to cause the preform to consolidate.
Dependencies are inferred from the claim text.