Rare earth and alumina-doped optical fiber preform process
AssigneeCorning Incorporated
InventorsCarl E. Crossland, Gang Qi
Life of this patent
Estimating the term…
Abstract
The present invention discloses novel methods for fabricating optical fiber glass preforms which may contain alumina, germania, erbium, or other rare earth metals as dopants. Doping with a higher concentration of alumina enhances the solubility of the erbium, or other rare earth, dopant within the glass and the resultant optical properties of the fiber. However, the addition of an alumina dopant can cause processing difficulties due to the formation of inclusions, such as gas bubble, seeds or crystallite formation, within the glass preform or glass cane. The present invention overcomes these processing difficulties and produces glass preforms or canes that are inclusion-free.
Claims10
A method for manufacturing an alumina-containing glass article that is substantially free of inclusions, said method comprising the steps of:
- a. forming soot through oxidation of glass constituent vapors and oxygen gas by exposure to a heat source within a reaction zone, wherein one of said glass constituent vapors is produced by sublimation of an aluminum-containing material at a sublimation temperature range of about 130° C. to about 170° C. and transported by a carrier gas to said reaction zone;
- b. consolidating said soot at a sintering temperature sufficient to sinter said soot into a glass blank;
- c. drawing the glass blank by heating at least one end of said glass blank to a first temperature to produce a precursor of a certain diameter;
- and
- d. re-drawing the precursor by heating at least one end of said precursor to a second temperature to produce an alumina-containing glass article of a certain diameter, said article having a diameter less than that of said precursor,
- wherein the heat source, in said forming step, is a burner that traverses across said soot at a rate of about 2.5 to about 3.5 cm/sec.
A method of producing an alumina-containing optical fiber waveguide perform that is substantially free of inclusions, said method comprising the steps of:
- a. heating glass constituents to a temperature sufficient to transform said constituents into a vapor, such that at least one of said glass constituents
- contains aluminum which is sublimated at a temperature range of about 130° C. to about 170° C.;
- b. transporting said vapor via a carrier gas to a reaction zone;
- c. reacting said vapor by exposing said vapor to a heat source to form a soot blank;
- d. consolidating said soot blank at a temperature sufficient to form a glass blank substantially free from particle boundaries;
- e. drawing said glass blank by heating at least one end of said blank to a first temperature to produce a precursor of a certain diameter;
- and
- f. re-drawing the precursor by heating at least one end of said precursor to a second temperature to produce a perform having a certain diameter, said perform having a diameter less than that of said precursor,
- wherein said heat source, in said reacting step, traverses said soot blank at a rate between about 2.5 cm/sec to about 3.5 cm/sec.
Dependencies are inferred from the claim text.