Method for establishing ultra-thin gate insulator using anneal in ammonia
AssigneeAdvanced Micro Devices, Inc.
InventorEffiong Ibok
Life of this patent
Estimating the term…
Abstract
A method for fabricating a semiconductor device including a silicon substrate includes forming a thin Oxide base film on a substrate, and then annealing the substrate in ammonia. FET gates are then conventionally formed over the gate insulator. The resultant gate insulator is electrically insulative without degrading performance with respect to a conventional gate oxide insulator.
Claims3
A method for making a semiconductor device, having an ultra-thin insulator for inhibiting tunneling effects, said method comprising:
- providing a semiconductor substrate;
- establishing an oxide base film on the substrate, said oxide base film having an oxide base film thickness, wherein said step of establishing the oxide base film comprises said oxide film thickness being in the range of no more than twenty-four Angstroms (≦24 Å);
- annealing the oxide base film on the substrate in an ammonia (NH3) environment in a temperature range of up to eleven hundred degrees Celsius (1100° C.), thereby forming a nitrided oxide film,
- wherein the step of annealing reduces the effective electrical thickness of the nitrided oxide film to twenty Angstroms (20 Å),
- said nitrided oxide film having a nitrided oxide film thickness being relative to said oxide base film thickness for facilitating inhibition of said tunneling effects, thereby resulting in a lower standby current for a higher drive current and capacitance, for facilitating function as a gate insulator, and for facilitating integration of said device,
- said nitrided oxide film having electrically insulating properties equal to that of an oxide film thinner than said oxide base film thickness, and
- said ultra-thin insulator comprising said nitrided oxide film;
- and
- forming at least one polysilicon-based field effect transistor (FET) gate on at least one portion of the nitrided oxide film.
A method for making a semiconductor device, having an ultra-thin insulator for inhibiting tunneling effects, said method comprising:
- providing a semiconductor substrate;
- establishing an oxide base film on the substrate, said oxide base film having an oxide base film thickness;
- annealing the oxide base film on the substrate in an ammonia (NH3) environment in a temperature range of up to eleven hundred degrees Celsius (1100° C.), thereby forming a nitrided oxide film, said nitrided oxide film having a nitrided oxide film thickness being relative to said oxide base film thickness,
- said nitrided oxide film having electrically insulating properties equal to that of an oxide film thinner than said oxide base film thickness, and
- said ultra-thin insulator comprising said nitrided oxide film;
- and
- forming at least one polysilicon-based field effect transistor (FET) gate at least one portion of the nitrided oxide film,
- wherein said step of establishing the oxide base film comprises said oxide film thickness being in a range of no more than twenty-four Angstroms (≦24 Å),
- wherein the step of annealing reduces an effective electrical thickness of the nitrided oxide film,
- wherein the step of annealing reduces the effective electrical thickness of the nitrided oxide film to twenty Angstroms (20 Å), and
- wherein the step of annealing decreases subsequent electron tunneling through the nitrided oxide film, thereby resulting in a lower standby current for higher drive current and capacitance than the oxide base film would have.