US 6,441,114 B1Granted
Adhesives for use on fluorine-containing or polycarbonate surfaces
Assignee3M Innovative Properties Company
InventorsRichard L. Peloquin, Albert I. Everaerts, Ellen O. Aeling
Life of this patent
Estimating the term…
Abstract
Adhesives useful in applying articles, such as tapes, labels, signs, decals, emblems, car moldings, protective or optical films, etc., to surfaces to which articles normally do not adhere well, such as surfaces containing fluorine and polycarbonate, for example. The adhesives include a copolymer of one or more monoethylenically unsaturated alkyl (meth)acrylate monomers, one or more monoethylenically unsaturated secondary or tertiary amide-functional monomers, and optionally one or more acidic monomers.
Claims20
A pressure sensitive adhesive comprising a copolymer comprising:
- at least one copolymerized monoethylenically unsaturated (meth)acrylic acid ester comprising an alkyl group having at least 4 carbons on average;
- at least one copolymerized monoethylenically unsaturated (meth)acrylic acid ester comprising an alkyl group having less than 4 carbons on average and which has a Tg of less than 50° C. as a homopolymer;
- and
- greater than 10 parts by weight, based on the total weight of monomers, of at least one copolymerized monoethylenically unsaturated monomer having a secondary or tertiary amide group of the formula —C(O)NR1R2 wherein R1 and R2 are each independently H or a saturated or unsaturated hydrocarbon moiety, which optionally forms a ring with the carbonyl carbon (—C(O)) of the amide group;
- wherein the pressure sensitive adhesive is removable, repositionable, or both within an initial period of about 24 hours and has a Tg of no greater than −15° C.
2 more elements
A pressure sensitive adhesive comprising a copolymer comprising:
- at least one copolymerized monoethylenically unsaturated (meth)acrylic acid ester comprising an alkyl group having at least 4 carbons on average;
- at least one copolymerized monoethylenically unsaturated (meth)acrylic acid ester comprising an alkyl group having less than 4 carbons on average and which has a Tg of less than 50° C. as a homopolymer;
- and
- greater than 10 parts by weight, based on the total weight of monomers, of at least one copolymerized monoethylenically unsaturated monomer having a secondary or tertiary amide group of the formula —C(O)NR1R2 wherein R1 and R2 are each independently H or a saturated or unsaturated hydrocarbon moiety, which optionally forms a ring with the carbonyl carbon (—C(O)) of the amide group;
- wherein all of the copolymerized monoethylenically unsaturated (meth)acrylic acid esters of the copolymer have a Tg of less than 50° C. as a homopolymer;
- wherein the pressure sensitive adhesive is removable, repositionable, or both within an initial period of about 24 hours and has a Tg of no greater than −15° C.
3 more elements
A pressure sensitive adhesive comprising a copolymer comprising:
- about 10 parts to about 70 parts by weight, based on the total weight of monomers, of at least one copolymerized monoethylenically unsaturated (meth)acrylic acid ester comprising an alkyl group having at least 4 carbons on average;
- about 20 parts to about 80 parts by weight, based on the total weight of monomers, of at least one copolymerized monoethylenically unsaturated (meth)acrylic acid ester comprising an alkyl group having less than 4 carbons on average and which has a Tg of less than 50° C. as a homopolymer;
- and
- greater than 10 parts and up to about 50 parts by weight, based on the total weight of monomers, of at least one copolymerized monoethylenically unsaturated monomer having a secondary or tertiary amide group of the formula —C(O)NR1R2 wherein R1 and R2 are each independently H or a saturated or unsaturated hydrocarbon moiety, which optionally forms a ring with the carbonyl carbon (—C(O)) of the amide group;
- wherein the pressure sensitive adhesive is removable, repositionable, or both within an initial period of about 24 hours and has a Tg of no greater than −15° C.
2 more elements
A pressure sensitive adhesive comprising a copolymer comprising:
- at least one copolymerized monoethylenically unsaturated (meth)acrylic acid ester comprising an alkyl group having at least 4 carbons on average and which as a homopolymer has a Tg of less than about 0° C.;
- at least one copolymerized monoethylenically unsaturated (meth)acrylic acid ester comprising an alkyl group having less than 4 carbons on average and which as a homopolymer has a Tg of less than 50° C.;
- and
- greater than 10 parts by weight, based on the total weight of monomers, at least one copolymerized monoethylenically unsaturated monomer having a secondary or tertiary arnide group of the formula —C(O)NR1R2 wherein R1 and R2 are each independently H or a saturated or unsaturated hydrocarbon moiety, which optionally forms a ring with the carbonyl carbon (—C(O)) of the amide group;
- wherein a 50-micron thick polymeric plasticized vinyl film having a 35-micron thick layer of the pressure sensitive adhesive disposed thereon has a 180° peel adhesion value of no greater than about 35 N/100 mm, measured at a 30.5 cm per minute peel rate, from a surface comprising an 80/20 polyvinylidenefluoride/polymethylmethacrylate blend after contact for 24 hours at 22° C., and after 7 days at 66° C. has a 180° peel adhesion value of at least about 70 N/100 mm, measured at a 30.5 cm per minute peel rate;
- and
- wherein the pressure sensitive adhesive has a Tg of no greater than −15° C.
4 more elements
A pressure sensitive adhesive comprising a copolymer comprising:
- at least one copolymerized monoethylenically unsaturated (meth)acrylic acid ester comprising an alkyl group having at least 4 carbons on average;
- at least one copolymerized monoethylenically unsaturated (meth)acrylic acid ester comprising an alkyl group having less than 4 carbons on average;
- and
- greater than 10 parts by weight, based on the total weight of monomers, of at least one copolymerized monoethylenically unsaturated monomer having a secondary or tertiary amide group selected from the group consisting of N,N-dimethyl acrylamide, N,N-diethyl acrylamide, N-vinyl pyrrolidone, and N-vinyl caprolactam, and combinations thereof;
- wherein all of the copolymerized monoethylenically unsaturated (meth)acrylic acid esters of the copolymer have a Tg of less than 50° C. as a homopolymer;
- and
- wherein the pressure sensitive adhesive has a Tg of no greater than −15° C.
4 more elements
A pressure sensitive adhesive comprising a copolymer comprising:
- at least one copolymerized monoethylenically unsaturated (meth)acrylic acid ester comprising an alkyl group having at least 4 carbons on average having a Tg of less than 0° C. as a homopolymer;
- at least one copolymerized monoethylenically unsaturated (meth)acrylic acid ester comprising an alkyl group having less than 4 carbons on average having a Tg of less than 50° C. as a homopolymer;
- and
- greater than 10 parts by weight, based on the total weight of monomers, of at least one copolymerized monoethylenically unsaturated monomer having a secondary or tertiary amide group of the formula —C(O)NR1R2 wherein R1 and R2 are each independently H or a saturated or unsaturated hydrocarbon moiety, which optionally forms a ring with the carbonyl carbon (—C(O)) of the amide group;
- wherein a 50-micron thick polymeric plasticized vinyl film having a 35-micron thick layer of the adhesive disposed thereon has a 180° peel adhesion value of no greater than about 35 N/100 mm, measured at a 30.5 cm per minute peel rate, from a surface comprising an 80/20 polyvinylidenefluoride/polymethylmethacrylate blend after contact for 24 hours at 22° C.;
- and
- wherein the pressure sensitive adhesive has a Tg of no greater than −15° C.
4 more elements
A pressure sensitive adhesive comprising a copolymer comprising:
- at least one copolymerized monoethylenically unsaturated (meth)acrylic acid ester comprising an alkyl group having at least 4 carbons on average having a Tg of less than 0° C. as a homopolymer;
- at least one copolymerized monoethylenically unsaturated (meth)acrylic acid ester comprising an alkyl group having less than 4 carbons on average having a Tg of less than 50° C. as a homopolymer;
- and
- greater than 10 parts by weight, based on the total weight of monomers, of at least one copolymerized monoethylenically unsaturated monomer having a secondary or tertiary amide group of the formula —C(O)NR1R2 wherein R1 and R2 are each independently H or a saturated or unsaturated hydrocarbon moiety, which optionally forms a ring with the carbonyl carbon (—C(O)) of the amide group;
- wherein a 50-micron thick polymeric plasticized vinyl film having a 35-micron thick layer of the adhesive disposed thereon has a 180° peel adhesion value of at least about 70 N/100 mm, measured at a 30.5 cm per minute peel rate, from a surface comprising an 80/20 polyvinylidenefluoride/polymethylmethacrylate blend after contact for 7 days at 66° C.;
- and
- wherein the pressure sensitive adhesive has a Tg of no greater than −15° C.
4 more elements
A pressure sensitive adhesive comprising a copolymer comprising:
- at least one copolymerized monoethylenically unsaturated (meth)acrylic acid ester comprising an alkyl group having at least 4 carbons on average;
- at least one copolymerized monoethylenically unsaturated (meth)acrylic acid ester comprising an alkyl group having less than 4 carbons on average and which has a Tg of less than 50° C. as a homopolymer;
- and
- greater than 10 parts by weight, based on the total weight of monomers, of at least one copolymerized monoethylenically unsaturated monomer having a secondary or tertiary amide group of the formula —C(O)NR1R2 wherein R1 and R2 are each independently H or a saturated or unsaturated hydrocarbon moiety, which optionally forms a ring with the carbonyl carbon (—C(O)) of the amide group, and further wherein at least one of R1 or R2 is a vinyl group;
- and
- wherein the pressure sensitive adhesive has a Tg of no greater than −15° C.