Multifunctional poly(vinyl alcohol) binder for fine particle size calcium carbonate pigment
AssigneeCelanese International Corporation
InventorJohn Richard Boylan
Life of this patent
Estimating the term…
Abstract
Production of a paper coating composition having improved low shear viscosity at a high solids level of fine particle size calcium carbonate. The improvement in low shear viscosity is achieved by dissolving a fine particle size, partially hydrolyzed, low molecular weight poly(vinyl alcohol) powder in an aqueous slurry of pigment particles containing predominantly fine particle size calcium carbonate. Dissolution of the poly(vinyl alcohol) is achieved without external heating or adding water to the slurry. The slurry can then be formulated with other components to produce the ink jet paper coating composition which, when applied to a paper substrate, provides excellent ink jet printability.
Claims3
A method of lowering the viscosity of an aqueous dispersion of fine particle size calcium carbonate 20 to 30% solids, having a mean surface area of at least 60 m2/g for use in a paper coating composition comprising adding to said aqueous dispersion poly(vinyl alcohol) in an amount of from 0.1 to 50 parts by weight poly(vinyl alcohol) per 100 parts calcium carbonate, the poly(vinyl alcohol) having a degree of polymerization of 150 to 300 and beinig 87 to 89 mole % hydrolyzed, and the poly(vinyl alcohol) particles having an average particle size of 180 μm or less.
Dependencies are inferred from the claim text.