Catalyst for purifying exhaust gases, a method of producing the same, and a method of purifying exhaust gases
AssigneeToyota Jidosha Kabushiki Kaisha
InventorsHirohito Hirata, Shinji Tsuji
Life of this patent
Estimating the term…
Abstract
A noble metal composite colloid composed of a plurality of noble metals is constructed to be loaded on a porous oxide support. The noble metals are loaded in particles which are larger than the conventional grains in the atomic state. Thus, vapor pressure decreases and volatile components, such as PtO2, are suppressed from dislocation or diffusion. In addition, affinity of the noble metals with the support is improved, and are suppressed from moving on the support. Thus, nobel metal grain growth is suppressed, decreases in catalytic activity is minimized and durability is improved.
Claims6
A catalyst for purifying exhaust gases, characterized in being produced by loading on a porous oxide support a noble metal composite colloid composed of a plurality of noble metals, wherein the noble metals of the noble metal colloid composite are present as particles between 1 to 5 nm, and an NOx storage component selected from the group consisting of alkali metals, alkaline-earth metals and rare-earth elements.
A catalyst for purifying exhaust gases, characterized in being produced by loading a noble metal composite colloid composed of a plurality of noble metals, wherein the noble metals of the noble metal colloid composite are present as particles between 1 to 5 nm, on the surface of a porous oxide support, and loading an atomic-state noble metal in micro pores of said porous oxide support.
A catalyst for purifying exhaust gases, characterized in being produced by loading on the surface of a porous oxide support a noble metal composite colloid composed of a plurality of noble metals, wherein the noble metals of the noble metal colloid composite are present as particles between 1 to 5 nm, and an NOx storage component selected from the group consisting of alkali metals, alkaline-earth metals and rare-earth elements, and loading in micro pores of said porous oxide support a noble metal in the atomic state and said NOx storage component.
A method of producing an exhaust-gases-purifying catalyst, characterized in comprising:
- a separation step of taking a noble metal composite colloid out of a polymer-protected noble metal composite colloid which is composed of a plurality of noble metals and protected by a polymeric material;
- a solution preparation step of dispersing said noble metal composite colloid in water by using a surfactant so as to prepare a surfactant-protected noble metal composite colloidal solution;
- a noble-metal-colloid-loading step of bringing a porous oxide support in contact with said surfactant-protected noble metal composite colloidal solution so as to load a surfactant-protected noble metal composite colloid on said porous oxide support;
- and
- an atomic-state-noble-metal-loading step of bringing said porous oxide support in contact with an aqueous solution of pyromellitic acid and a noble metal compound so as to load an atomic-state noble metal on said porous oxide support.
A method of purifying exhaust gases, characterized in placing, in exhaust gases in oxygen-excessive atmospheres, a catalyst produced by loading on a porous oxide support a noble metal composite colloid composed of a plurality of noble metals, wherein the noble metals of the noble metal colloid composite are present as particles between 1 to 5 nm, and an NOx storage component selected from the group consisting of alkali metals, alkaline-earth metals and rare-earth elements so as to adsorb NOx in said exhaust gases on said NOx storage component, and changing the exhaust gas atmospheres to a stoichiometric point or on a fuel-rich side so as to release said NOx from said NOx storage component and reduce said NOx.
Dependencies are inferred from the claim text.