Adhesive film for semiconductor package
AssigneeNisshinbo Industries, Inc.
InventorsYasuo Imashiro, Takahiko Ito, Hideshi Tomita, Norimasa Nakamura
Life of this patent
Estimating the term…
Abstract
The present invention provides an adhesive film for semiconductor package, which comprises a polycarbodiimide resin, an epoxy resin and an inorganic filler, wherein the polycarbodiimide resin has a polystyrene-reduced number-average molecular weight of 3,000 to 50,000 as measured by gel permeation chromatography, the epoxy resin is contained in an amount of 20 to 150 parts by weight per 100 parts by weight of the polycarbodiimide resin, and the inorganic filler is contained in an amount of 30 to 70% by weight based on the total resin content.
Claims4
An adhesive film for semiconductor package, which comprises a polycarbodiimide resin, an epoxy resin and an inorganic filler, wherein the polycarbodiimide resin has a polystyrene-reduced number-average molecular weight of 3,000 to 50,000 as measured by gel permeation chromatography, the epoxy resin is contained in an amount of 40 to 130 parts by weight per 100 parts by weight of the polycarbodiimide resin, and the inorganic filler is contained in an amount of 30 to 70% by weight based on the total resin content.
A method for adhering components of a semiconductor package comprising:
- a) providing an adhesive film for semiconductor package which comprises a polycarbodiimide resin, an epoxy resin and an inorganic filler, wherein the polycarbodiimide resin has a polystyrene-reduced number-average molecular weight of 3,000 to 50,000 as measured by gel permeation chromatography, the epoxy resin is contained in an amount of 40 to 130 parts by weight per 100 parts by weight of the polycarbodiimide resin, and the inorganic filler is contained in an amount of 30 to 70% by weight based on the total resin content;
- b) interposing said adhesive film for semiconductor package between components of a semiconductor package to obtain a precursor semiconductor package;
- and
- c) heat treating the precursor semiconductor package at a temperature of 150 to 300° C. and a pressure of 0.1 to 5 Kg/cm2 for a period of 5 seconds to 10 minutes.
Dependencies are inferred from the claim text.