Procedure for adding a filler into a pulp based on cellulose fibers
AssigneeM-real Oyj
InventorsPetri Silenius, Markku Leskelä, Johan Gullichsen, Esa Halinen
Life of this patent
Estimating the term…
Abstract
The invention relates to a procedure for adding a filler into a pulp based on cellulose fibers, in which the pulp is fluidized and the filler is added into it. Preferably the pulp is stirred in the fluidized state while the filler is being added. The pulp is preferably at a medium consistency when the filler is being added. Preferably the filler added into the pulp is calcium hydroxide and the calcium carbonate is precipitated with carbon dioxide.
Claims11
Method for adding a filler into a pulp based on cellulose fibers, comprising:
- fluidizing the pulp;
- adding calcium hydroxide to the fluidized pulp to form a mixture;
- and
- adding carbon dioxide while stirring the mixture in fluidized state for precipitating calcium carbonate as the filler in pores and lumens of the fibers.
Method for adding a filler into a pulp based on cellulose fibers, comprising:
- fluidizing the pulp;
- adding calcium hydroxide to the fluidized pulp to form a mixture;
- and
- adding a stoichiometric amount of carbon dioxide required for reaction at a pressure of 1-20 bar while stirring the mixture in fluidized state for precipitating calcium carbonate as the filler in pores and lumens of the fibers,
- wherein a mass ratio of calcium hydroxide and cellulose fibers during precipitation is 0.1-0.3 and a precipitation temperature is 10-90° C., and wherein a consistency of the pulp is 5-18 w-% when adding calcium hydroxide and carbon dioxide.
Method for producing porous calcium carbonate aggregates to be used in paper manufacture, comprising:
- fluidizing cellulose-fiber based fine material;
- adding calcium hydroxide to the fluidized cellulose-fiber based fine material to form a mixture;
- and
- adding a stoichiometric amount of carbon dioxide required for reaction at a pressure of 1-20 bar while stirring the mixture in fluidized state for precipitating calcium carbonate in pores and lumens of the fine material, wherein a mass ratio of calcium hydroxide and fine material during precipitation is 0.14-0.4 and a precipitation temperature is 10-90° C., and wherein a consistency of the pulp is 5-18 w-% when adding calcium hydroxide and carbon dioxide.
Dependencies are inferred from the claim text.