High energy density metallized film capacitors and methods of manufacture thereof
AssigneeLithium Power Technologies, Inc.
InventorM. Zafar A. Munshi
Life of this patent
Estimating the term…
Abstract
A film capacitor includes a novel hybrid polymeric film dielectric in which at least one non-polar dielectric homopolymer resin is blended homogeneously in solid-solution with at least one other dielectric polymer resin. The properties of at least one of the dielectric polymer resin constituents of the hybrid polymeric film dielectric are selected to produce a tailored property or properties of the solid-solution blend thereof. The non-polar homopolymer serves to stabilize the hybrid polymeric film. In the film capacitor configuration, the hybrid polymeric film is tightly sandwiched between conformable metal plates.
Claims56
A dielectric film with values of at least some electrical properties thereof among dielectric constant, dielectric strength, stability, breakdown voltage, dissipation factor, clearability, and insulation resistance optimized for usage of said dielectric film in a film capacitor, said dielectric film comprising a melt-cast substantially homogeneous hybrid copolymer solid-solution blend of at least one non-polar homopolymer and at least one other homopolymer, in which the specific designation and concentration of each of said homopolymers in said blend are selected for tailoring said properties of the dielectric film to achieve said optimization.
A dielectric film with values of at least some properties thereof among dielectric constant, dielectric strength, stability, breakdown voltage, dissipation factor, clearability, insulation resistance, and operating temperature optimized for usage of said dielectric film in a film capacitor, said dielectric film comprising a melt-cast hybrid copolymer solid-solution blend of at least one non-polar homopolymer and at least one other homopolymer, wherein said homopolymers include at least polypropylene (PP) and polyvinylidenefluoride (PVDF) in a concentration range from 0.99 to 0.01 PVDF, with the balance PP, in which the specific designation and concentration of each of said homopolymers in said blend are selected for tailoring said properties of the dielectric film to achieve said optimization.
A dielectric film for a dry film capacitor, comprising a melt-cast hybrid copolymer solid-solution blend of at least one homopolymer selected to have non-polar characteristics to stabilize said film, and at least one polar homopolymer, each of said homopolymers having at least one predetermined property for which its presence and its concentration in the blend are selected to offset a weak property of the other homopolymer and thereby tailor a selected property of said dielectric film toward a desired value from among properties of dielectric constant, dielectric strength, stability, breakdown voltage, dissipation factor, clearability, insulation resistance, and operating temperature.
A dielectric film comprising a melt-cast hybrid copolymer solid-solution blend of at least one non-polar homopolymer selected to stabilize said film, and at least one other homopolymer having a predetermined property selected to enhance the same property of said dielectric film from among properties of dielectric constant, dielectric strength, stability, breakdown voltage, dissipation factor, clearability, insulation resistance, and operating temperature, wherein said homopolymers are polypropylene (PP) and polyvinylidenefluoride (PVDF) in a concentration ratio of from 99% to 1% PVDF to from 1% to 99% PP by weight, respectively.
A dry film capacitor comprising:
- a melt-cast hybrid copolymeric dielectric film composed of a homogeneous solid-solution blend of at least one homopolymer selected to have non-polar characteristics to stabilize said film, with at least one polar homopolymer, each of said homopolymers having properties and concentrations in said blend selected to tailor at least one predetermined property of said dielectric film toward a desired value from among properties including dielectric constant, dielectric strength, stability, breakdown voltage, dissipation factor, clearability, insulation resistance, and operating temperature, and
- a pair of spaced-apart metal films between which said dielectric film is tightly sandwiched.
A film capacitor comprising:
- a melt-cast hybrid copolymeric dielectric film composed of a homogeneous solid-solution blend of at least one non-polar homopolymer with at least one other homopolymer, said homopolymers having properties and concentrations in said blend selected to tailor at least one predetermined property of said dielectric film from among properties including dielectric constant, dielectric strength, stability, breakdown voltage, dissipation factor, clearability, insulation resistance, and operating temperature, wherein said homopolymers are polypropylene (PP) and polyvinylidenefluoride (PVDF) in volume concentrations of from 99% to 1% PVDF, and the balance PP, and
- a pair of spaced-apart metal films between which said dielectric film is tightly sandwiched, wherein said film capacitor has an energy density exceeding 5 Joules per cubic centimeter.
An improved polymeric film of high dielectric constant and dielectric strength, high stability and low dissipation factor, comprising:
- a hybrid solid-solution blend of homopolymers of high purity polyvinylidenefluoride (PVDF) and polypropylene (PP) resins in a concentration ratio of PVDF:PP ranging from 1% to 99 % PVDF and the balance PP, said concentration ratio being selected to tailor properties of said film including dielectric constant, dielectric strength, stability and dissipation factor,
- said film being bi-axially oriented with a thickness in a range from about 0.5 μm to 25 μm, and having a polymeric coating with properties of dielectric constant and stability selected to seal defects and provide limited hardening of the surface of said film.
A metallized film capacitor having an energy density exceeding 5 Joules per cubic centimeter, comprising:
- a dielectric film composed of a melt-cast hybrid copolymer solid-solution blend of homopolymers of high purity polyvinylidenefluoride (PVDF) and polypropylene (PP) resins in concentrations ranging from 1% to 99% PVDF and the balance PP selected to tailor at least one of the properties of said dielectric film including dielectric constant, dielectric strength, stability, breakdown voltage, dissipation factor, clearability, insulation resistance, and operating temperature, said dielectric film having bi-axial orientation and a thickness in a range from about 0.5 μm to 25 μm,
- a polymeric coating on said dielectric film having properties of dielectric constant and stability selected to seal defects and provide limited hardening of the surface of said dielectric film,
- one major surface of the coated dielectric film being metallized, the metallized coated film being wound with an unmetallized major surface thereof opposite said one major surface in tight contact with a metallized major surface of a corresponding metallized coated dielectric film to form said capacitor with a predetermined capacitance value.
Method of manufacturing a metallized film capacitor, comprising the steps of:
- selecting at least two homopolymers of high purity, capacitor grade polymeric resins according to desired properties of a dielectric film for said metallized film capacitor including dielectric constant, dielectric strength, stability, breakdown voltage, dissipation factor, clearability, insulation resistance, and operating temperature;
- forming a melt-cast hybrid copolymer homogeneous blend of said at least two homopolymers into a thin dielectric film;
- bi-axially orienting said thin dielectric film by stretching thereof with a machine direction orientation to a thickness in a range from about 25 to about 50 microns and thereafter stretching said film in a transverse direction orientation to a thickness in a range from about 0.5 to about 25 microns;
- coating said biaxially oriented dielectric film with a polymeric material selected to seal defects in and to at least slightly harden the surface of said film;
- applying an adherent layer of metal having an electrical resistance in a range from about 0.1 ohm to about 1000 ohms per square onto one major surface of the coated dielectric film;
- and
- tightly winding the metallized coated dielectric film with another correspondingly formed metallized coated dielectric film with an unmetallized major surface of one abutting a metallized major surface of the other, to provide said metallized film capacitor with a desired capacitance value.
Method of manufacturing a dielectric film, comprising the steps of:
- homogeneously blending into a solid-solution blend at least two homopolymers of high purity polymeric resins with properties and in concentrations preselected to tailor said dielectric film toward desired values of properties from among dielectric constant, dielectric strength, stability, breakdown voltage, dissipation factor, clearability, insulation resistance, and operating temperature of the film;
- forming a melt-cast hybrid copolymer dielectric film from the homogeneously blended homopolymers;
- and
- bi-axially orienting said melt-cast hybrid copolymer dielectric film by stretching it in a machine direction orientation and a transverse direction orientation, to achieve a desired final film thickness.
Method of manufacturing a dielectric film, comprising the steps of:
- homogeneously blending into a solid-solution blend at least two homopolymers of high purity polymeric resins with properties and in concentrations preselected to provide said dielectric film with desired properties from among dielectric constant, dielectric strength, stability, breakdown voltage, dissipation factor, clearability, insulation resistance, and operating temperature of the film, wherein said at least two homopolymers are polyvinylidenefluoride (PVDF) and polypropylene (PP);
- forming a melt-cast hybrid copolymer dielectric film from the homogeneously blended homopolymers;
- and
- bi-axially orienting said melt-cast hybrid copolymer dielectric film by stretching it in a machine direction orientation and a transverse direction orientation, to achieve a desired final film thickness.
Method of manufacturing a dielectric film, comprising the steps of:
- homogeneously blending into a solid-solution blend at least two homopolymers of high purity polymeric resins with properties and in concentrations preselected to provide said dielectric film with desired properties from among dielectric constant, dielectric strength, stability, breakdown voltage, dissipation factor, clearability, insulation resistance, and operating temperature of the film;
- forming a melt-cast hybrid copolymer dielectric film from the homogeneously blended homopolymers;
- bi-axially orienting said melt-cast hybrid copolymer dielectric film by stretching it in a machine direction orientation and a transverse direction orientation, to achieve a desired final film thickness;
- and
- coating said bi-axially oriented film with polymeric material selected to seal defects in and to at least slightly harden the surface of said dielectric film.
A polymeric film for use as a dielectric in a film capacitor, said polymeric film comprising:
- a hybrid copolymer solid-solution blend, including
- a first component having at least one of electrical properties among dielectric constant, dielectric strength, stability, breakdown voltage, dissipation factor, clearability, and insulation resistance with an intrinsic value that renders said first component highly suitable as a dielectric in the film capacitor, and having at least another of said electrical properties with an intrinsic value that detracts from the suitability of said first component as a dielectric in the film capacitor, and
- a second component having said another electrical property with an intrinsic value that renders said second component highly suitable as a dielectric in the film capacitor,
- the relative proportions of said first and second components of said hybrid copolymer solid-solution blend being selected to produce an optimum value of said another electrical property in the blend for the film capacitor application.
A dielectric film comprising a melt-cast hybrid copolymer solid-solution blend of at least two polymeric constituents, one of said constituents having an electrical property among dielectric constant, dielectric strength, stability, breakdown voltage, dissipation factor, clearability, and insulation resistance, with a value that renders said one constituent desirable for a predetermined capacitor application and having another among said electrical properties with a value that renders said one constituent unsuitable for said predetermined capacitor application;
- and another of said constituents selected for its value of said another electrical property to enhance said another electrical property of the overall blend for said predetermined capacitor application.
A film capacitor comprising:
- a melt-cast hybrid copolymer dielectric film composed of a homogeneous solid-solution blend comprising two polymeric constituents,
- one of said two constituents having an electrical property among dielectric constant, dielectric strength, stability, breakdown voltage, dissipation factor, clearability, and insulation resistance, with a value that renders said one constituent desirable for a predetermined application of said film capacitor and having another among said electrical properties with a value that renders said one constituent unsuitable for said predetermined application, and
- the other of said two constituents selected for its value of said another electrical property to enhance said another electrical property of the overall blend sufficiently to overcome the unsuitability of said one constituent for said predetermined application;
- and
- a pair of spaced-apart metal films between which said dielectric film is tightly sandwiched.
Method of manufacturing a polymeric film for a film capacitor, comprising the steps of:
- blending at least two polymer resin components to form a hybrid copolymer solid-solution, including
- selecting one of said components for an electrical property among dielectric constant, dielectric strength, stability, breakdown voltage, dissipation factor, clearability, and insulation resistance with an intrinsic value that renders said one component highly suitable for inclusion in the film capacitor, but having another of said electrical properties with an intrinsic value that detracts from the suitability of said one component for inclusion in the film capacitor,
- selecting the other of said components for its having said another electrical property of desirable intrinsic value for inclusion in the film capacitor, and
- setting the relative proportions of said components in said blend to produce an optimum value of said another electrical property in the polymeric film for the film capacitor application.