β-titanium alloy wire, method for its production and medical instruments made by said β-titanium alloy wire
AssigneeTerumo Kabushiki Kaisha
InventorsNaoki Ishii, Takashi Kaneko, Shin Sumimoto, Hideki Yamamoto, Ichiro Nagao
Life of this patent
Estimating the term…
Abstract
The diamter of β-titanium alloy wire is reduced by cold wire-drawing and the β-titanium alloy wire is subjected to heat treatment. The heat treatment comprises the first aging process for precipitation strengthening and the second aging process for removing processing strain. β-titanium alloy wire is heat-treated under the supply of tension at the second aging process.
Claims4
β-titanium alloy wire comprising a diameter of 0.01 to 2.0 mm is characterized in that an average crystal grain area A of β-phase in cross section structure is 1 to 80 μm2, an average crystal grain length L of β-phase in vertical section structure is 10 to 1000 μm and a ratio of L/{square root over ( )}A is 5 to 1000.
A guide wire for medical treatment comprising β-titanium alloy wire that an average crystal grain area A of β-phase in cross section structure is 1 to 80 μm2, an average crystal grain length L of β-phase in vertical section structure is 10 to 1000 μm and a ratio of L/{square root over ( )}A is 5 to 1000.
A catheter comprising β-titanium alloy wire that an average crystal grain area A of β-phase in cross section structure is 1 to 80 μm2, an average crystal grain length L of β-phase in vertical section structure is 10 to 100 μm and a ratio of L/{square root over ( )}A is 5 to 1000.
A stent comprising β-titanium alloy wire that an average crystal grain area A of β-phase in cross section structure is 1 to 80 μm2, an average crystal grain length L of β-phase in vertical section structure is 10 to 1000 μm and a ratio of L/{square root over ( )}A is 5 to 1000.