Pitch-based carbon foam and composites
AssigneeUT-Battelle, LLC
InventorJames W. Klett
Life of this patent
Estimating the term…
Abstract
A process for producing carbon foam or a composite is disclosed which obviates the need for conventional oxidative stabilization. The process employs mesophase or isotropic pitch and a simplified process using a single mold. The foam has a relatively uniform distribution of pore sizes and a highly aligned graphic structure in the struts. The foam material can be made into a composite which is useful in high temperature sandwich panels for both thermal and structural applications.
Claims65
A graphitic carbon foam characterized by an X-ray diffraction pattern as depicted in FIG. 11.
A graphitic carbon foam characterized by an X-ray diffraction pattern exhibiting doublet peaks at 2θ angles between 40 and 50 degrees.
A graphitic carbon foam characterized by an x-ray diffraction pattern having an average d002 spacing of about 0.336 nm, wherein the x-ray diffraction pattern exhibits doublet peaks at 2θ angles between 40 and 50 degrees.
A graphitic carbon foam characterized by an x-ray diffraction pattern, wherein the average d002 spacing is 0.336 nm.
A graphitic carbon foam having a specific thermal conductivity of at least about 109 W·cm3/m·K·g.
A graphitic carbon foam having a specific thermal conductivity greater than four times that of copper.
A graphitic carbon foam characterized by an x-ray diffraction pattern as depicted in FIG. 11 and having a specific thermal conductivity greater than copper.
A graphitic carbon foam characterized by an x-ray diffraction pattern as depicted in FIG. 11 and having a bulk thermal conductivity from about 58 W/m·K to about 106 W/m·K.
A graphitic carbon foam characterized by an x-ray diffraction pattern as depicted in FIG. 11, the carbon foam having an open cell structure consisting essentially of ellipsoidal pores, said carbon foam having been derived from a pitch selected from the group consisting of synthetic mesophase pitch, synthetic isotropic pitch, petroleum-derived mesophase pitch, petroleum-derived isotropic pitch, and coal-tar-derived mesophase pitch.
A graphitic carbon foam characterized by an x-ray diffraction pattern as depicted in FIG. 11, said carbon foam having an open cell pore structure comprised of pores whose planar cross sectional images are circular or elliptical, said carbon foam having been derived from a pitch selected from the group consisting of synthetic mesophase pitch, synthetic isotropic pitch, petroleum-derived mesophase pitch, petroleum-derived isotropic pitch, and coal-tar-derived mesophase pitch.
A graphitic carbon foam characterized by an x-ray diffraction pattern as depicted in FIG. 11, wherein said carbon foam is non-oxidatively stabilized and of an open cell structure comprising cell walls wherein carbon in the form of graphite and derived from a mesophase pitch is aligned along the cell wall axes.
A graphitic carbon foam characterized by an x-ray diffraction pattern exhibiting doublet peaks at 2θ angles between 40 and 50 degrees and having a specific thermal conductivity greater than copper.
A graphitic carbon foam characterized by an x-ray diffraction pattern exhibiting doublet peaks at 2θ angles between 40 and 50 degrees and having a bulk thermal conductivity from about 58 W/m·K to about 106 W/m·K.
A graphitic carbon foam characterized by an x-ray diffraction pattern exhibiting doublet peaks at 2θ angles between 40 and 50 degrees, said carbon foam having an open cell pore structure consisting essentially of ellipsoidal pores, said carbon foam having been derived from a pitch selected from the group consisting of synthetic mesophase pitch, synthetic isotropic pitch, petroleum-derived mesophase pitch, petroleum-derived isotropic pitch, and coal-tar-derived mesophase pitch.
A graphitic carbon foam characterized by an x-ray diffraction pattern exhibiting doublet peaks at 2θ angles between 40 and 50 degrees, said carbon foam having an open cell pore structure comprised of pores whose planar cross sectional images are circular or elliptical, said carbon foam having been derived from a pitch selected from the group consisting of synthetic mesophase pitch, synthetic isotropic pitch, petroleum-derived mesophase pitch, petroleum-derived isotropic pitch, and coal-tar-derived mesophase pitch.
A graphitic carbon foam characterized by an x-ray diffraction pattern exhibiting doublet peaks at 2θ angles between 40 and 50 degrees, wherein said carbon foam is non-oxidatively stabilized and of an open cell structure comprising cell walls wherein carbon in the form of graphite and derived from a mesophase pitch is aligned along the cell wall axes.
A graphitic carbon foam characterized by an x-ray diffraction pattern having an average d002 spacing of 0.336 nm and having a specific thermal conductivity greater than copper.
A graphitic carbon foam characterized by an x-ray diffraction pattern having an average d002 spacing of 0.336 nm, said carbon foam having an open cell pore structure comprised of pores whose planar cross sectional images are circular or elliptical, said carbon foam having been derived from a pitch selected from the group consisting of synthetic mesophase pitch, synthetic isotropic pitch, petroleum-derived mesophase pitch, petroleum-derived isotropic pitch, and coal-tar-derived mesophase pitch.
A graphitic carbon foam having a specific thermal conductivity from about 109 W·cm3/m·K·g to about 200 W·cm3/m·K·g, said carbon foam having an open cell pore structure consisting essentially of ellipsoidal pores, and having been derived from a pitch selected from the group consisting of synthetic mesophase pitch, synthetic isotropic pitch, petroleum-derived mesophase pitch, petroleum-derived isotropic pitch, and coal-tar-derived mesophase pitch.
A graphitic carbon foam having a specific thermal conductivity from about 109 W·cm3/m·K·g to about 200 W·cm3/m·K·g, said carbon foam having an open cell pore structure comprised of pores whose planar cross sectional images are circular or elliptical, said carbon foam having been derived from a pitch selected from the group consisting of synthetic mesophase pitch, synthetic isotropic pitch, petroleum-derived mesophase pitch, petroleum-derived isotropic pitch, and coal-tar-derived mesophase pitch.
A graphitic carbon foam having a specific thermal conductivity from about 109 W·cm3/m·K·g to about 200 W·cm3/m·K·g, said carbon foam being non-oxidatively stabilized carbon foam of an open cell structure comprising cell walls wherein carbon in the form of graphite and derived from a mesophase pitch is aligned along the cell wall axes.
A graphitic carbon foam having a specific thermal conductivity greater than four times that of copper, said carbon foam having an open cell pore structure consisting essentially of ellipsoidal pores, said carbon foam having been derived from a pitch selected from the group consisting of synthetic mesophase pitch, synthetic isotropic pitch, petroleum-derived mesophase pitch, petroleum-derived isotropic pitch, and coal-tar-derived mesophase pitch.
A graphitic carbon foam having a specific thermal conductivity greater than four times that of copper, said carbon foam having an open cell pore structure comprised of pores whose planar cross sectional images are circular or elliptical, said carbon foam having been derived from a pitch selected from the group consisting of synthetic mesophase pitch, synthetic isotropic pitch, petroleum-derived mesophase pitch, petroleum-derived isotropic pitch, and coal-tar-derived mesophase pitch.
A graphitic carbon foam having a specific thermal conductivity greater than four times that of copper, said carbon foam being non-oxidatively stabilized and of an open cell structure comprising cell walls wherein carbon in the form of graphite and derived from a mesophase pitch is aligned along the cell wall axes.
A graphitic carbon foam having a bulk thermal conductivity from about 58 W/m·K to about 106 W/m·K and being characterized by an x-ray diffraction pattern as depicted in FIG. 11, said carbon foam having an open cell pore structure consisting essentially of ellipsoidal pores, said carbon foam having been derived from a pitch selected from the group consisting of synthetic mesophase pitch, synthetic isotropic pitch, petroleum-derived mesophase pitch, petroleum-derived isotropic pitch, and coal-tar-derived mesophase pitch.
A graphitic carbon foam having a bulk thermal conductivity from about 58 W/m·K to about 106 W/m·K and being characterized by an x-ray diffraction pattern as depicted in FIG. 11, said carbon foam having an open cell pore structure comprised of pores whose planar cross sectional images are circular or elliptical, said carbon foam having been derived from a pitch selected from the group consisting of synthetic mesophase pitch, synthetic isotropic pitch, petroleum-derived mesophase pitch, petroleum-derived isotropic pitch, and coal-tar-derived mesophase pitch.
A graphitic carbon foam having a bulk thermal conductivity from about 58 W/m·K to about 106 W/m·K and being characterized by an x-ray diffraction pattern as depicted in FIG. 11, said carbon foam being non-oxidatively stabilized and of an open cell structure comprising cell walls wherein carbon in the form of graphite and derived from a mesophase pitch is aligned along the cell wall axes.
A graphitic carbon foam having a specific thermal conductivity of at least about 109 W·cm3/m·K·g and being characterized by an x-ray diffraction pattern exhibiting doublet peaks at 2θ angles between 40 and 50 degrees, said carbon foam having an open cell pore structure consisting essentially of ellipsoidal pores, said carbon foam having been derived from a pitch selected from the group consisting of synthetic mesophase pitch, synthetic isotropic pitch, petroleum-derived mesophase pitch, petroleum-derived isotropic pitch, and coal-tar-derived mesophase pitch.
A graphitic carbon foam having a specific thermal conductivity of at least about 109 W·cm3/m·K·g and being characterized by an x-ray diffraction pattern exhibiting doublet peaks at 2θ angles between 40 and 50 degrees, said carbon foam having an open cell pore structure comprised of pores whose planar cross sectional images are circular or elliptical, said carbon foam having been derived from a pitch selected from the group consisting of synthetic mesophase pitch, synthetic isotropic pitch, petroleum-derived mesophase pitch, petroleum-derived isotropic pitch, and coal-tar-derived mesophase pitch.
A graphitic carbon foam having a specific thermal conductivity of at least about 109 W·cm3/m·K·g and being characterized by an x-ray diffraction pattern exhibiting doublet peaks at 2θ angles between 40 and 50 degrees, said carbon foam being non-oxidatively stabilized and of an open cell structure comprising cell walls wherein carbon in the form of graphite and derived from a mesophase pitch is aligned along the cell wall axes.
A graphitic carbon foam having a specific thermal conductivity from about 109 W·cm3/m·K·g to about 200 W·cm3/m·K·g and being characterized by an x-ray diffraction pattern having an average d002 spacing of about 0.336 nm, said carbon foam having an open cell pore structure consisting essentially of ellipsoidal pores, said carbon foam having been derived from a pitch selected from the group consisting of synthetic mesophase pitch, synthetic isotropic pitch, petroleum-derived mesophase pitch, petroleum-derived isotropic pitch, and coal-tar-derived mesophase pitch.
A graphitic carbon foam having a specific thermal conductivity from about 109 W·cm3m·K·g to about 200 W·cm3/m·K·g and being characterized by an x-ray diffraction pattern having an average d002 spacing of about 0.336 nm, said carbon foam having an open cell pore structure comprised of pores whose planar cross sectional images are circular or elliptical, said carbon foam having been derived from a pitch selected from the group consisting of synthetic mesophase pitch, synthetic isotropic pitch, petroleum-derived mesophase pitch, petroleum-derived isotropic pitch, and coal-tar-derived mesophase pitch.
A graphitic carbon foam having a specific thermal conductivity from about 109 W·cm3m·K·g to about 200 W·cm3/m·K·g and being characterized by an x-ray diffraction pattern having an average d002 spacing of about 0.336 nm, said carbon foam being non-oxidatively stabilized and of an open cell structure comprising cell walls wherein carbon in the form of graphite and derived from a mesophase pitch is aligned along the cell wall axes.
A graphitic carbon foam having a specific thermal conductivity greater than four times that of copper and being characterized by an x-ray diffraction pattern having an average d002 spacing of 0.336 nm, said carbon foam having an open cell pore structure consisting essentially of ellipsoidal pores, said carbon foam having been derived from a pitch selected from the group consisting of synthetic mesophase pitch, synthetic isotropic pitch, petroleum-derived mesophase pitch, petroleum-derived isotropic pitch, and coal-tar-derived mesophase pitch.
A graphitic carbon foam having a specific thermal conductivity greater than four times that of copper and being characterized by an x-ray diffraction pattern having an average d002 spacing of 0.336 nm, said carbon foam having an open cell pore structure comprised of pores whose planar cross sectional images are circular or elliptical, said carbon foam having been derived from a pitch selected from the group consisting of synthetic mesophase pitch, synthetic isotropic pitch, petroleum-derived mesophase pitch, petroleum-derived isotropic pitch, and coal-tar-derived mesophase pitch.
A graphitic carbon foam having a specific thermal conductivity greater than four times that of copper and being characterized by an x-ray diffraction pattern having an average d002 spacing of 0.336 nm, said carbon foam being non-oxidatively stabilized and of an open cell structure comprising cell walls wherein carbon in the form of graphite and derived from a mesophase pitch is aligned along the cell wall axes.
A graphitic carbon foam having a specific thermal conductivity greater than that of copper and being characterized by an x-ray diffraction pattern having an average d002 spacing of 0.336 nm, said carbon foam having an open cell pore structure consisting essentially of ellipsoidal pores, said carbon foam having been derived from a pitch selected from the group consisting of synthetic mesophase pitch, synthetic isotropic pitch, petroleum-derived mesophase pitch, petroleum-derived isotropic pitch, and coal-tar-derived mesophase pitch.
A graphitic carbon foam having a specific thermal conductivity greater than that of copper and being characterized by an x-ray diffraction pattern having an average d002 spacing of 0.336 nm, said carbon foam having an open cell pore structure comprised of pores whose planar cross sectional images are circular or elliptical, said carbon foam having been derived from a pitch selected from the group consisting of synthetic mesophase pitch, synthetic isotropic pitch, petroleum-derived mesophase pitch, petroleum-derived isotropic pitch, and coal-tar-derived mesophase pitch.
A graphitic carbon foam having a specific thermal conductivity greater than that of copper and being characterized by an x-ray diffraction pattern having an average d002 spacing of 0.336 nm, said carbon foam being non-oxidatively stabilized and of an open cell structure comprising cell walls wherein carbon in the form of graphite and derived from a mesophase pitch is aligned along the cell wall axes.
A graphitic carbon foam characterized by a specific thermal conductivity of at least about 109 W·cm3/m·K·g and an x-ray diffraction pattern having an average d002 spacing of 0.336 nm, said foam being pitch-derived and non-oxidatively stabilized said foam being further characterized by an open cell pore structure comprised of ellipsoidal pores and by graphite aligned along the axes of the cell walls.
A graphitic carbon foam characterized by a specific thermal conductivity of at least about 109 W·cm3/m·K·g and an x-ray diffraction pattern having an average d002 spacing of 0.336 nm, said carbon foam being a mesophase pitch-derived, non-oxidatively stabilized carbon foam characterized (1) by an open cell pore structure consisting essentially of pores whose planar cross sectional images are circular or elliptical and (2) by carbon aligned along the axes of the cell walls.
A graphitic carbon foam derived from a pitch selected from the group consisting of petroleum-derived mesophase pitch, coal-tar-derived mesophase pitch, and synthetic mesophase pitch, said carbon foam being further characterized by a specific thermal conductivity greater than four times that of copper and an x-ray diffraction pattern as depicted in FIG. 11, said foam being non-oxidatively stabilized and further characterized by an open cell pore structure comprised of ellipsoidal pores and by graphite aligned along the axes of the cell walls.
A graphitic carbon foam derived from a pitch selected from the group consisting of petroleum-derived mesophase pitch, coal-tar-derived mesophase pitch, and synthetic mesophase pitch, said carbon foam being freer characterized by a specific thermal conductivity greater than four times that of copper and an x-ray diffraction pattern as depicted in FIG. 11, said foam being non-oxidatively stabilized carbon foam and characterized (1) by an open cell pore structure consisting essentially of pores whose planar cross sectional images are circular or elliptical and (2) by carbon aligned along the axes of the cell walls.
A graphitic carbon foam wherein the x-ray diffraction pattern exhibits doublet peaks at 2θ angles between 40 and 50 degrees, said foam having a bulk thermal conductivity from about 58 W/m·K to about 106 W/m·K and an x-ray diffraction pattern having an average d002 spacing of about 0.336 nm, said foam being pitch-derived and non-oxidatively stabilized and further characterized by an open cell pore structure comprised of ellipsoidal pores and by graphite aligned along the axes of the cell walls.
A graphitic carbon foam wherein the x-ray diffraction pattern exhibits doublet peaks at 2θ angles between 40 and 50 degrees, said foam having a bulk thermal conductivity from about 58 W/m·K to about 106 W/m·K and an x-ray diffraction pattern having an average d002 spacing of about 0.336 nm, said foam being mesophase pitch-derived, non-oxidatively stabilized and characterized (1) by an open cell pore structure consisting essentially of pores whose planar cross sectional images are circular or elliptical and (2) by carbon aligned along the axes of the cell walls.
A graphitic carbon foam having a specific thermal conductivity of at least 109 W·cm3/m·K·g, said carbon foam having an open cell pore structure consisting essentially of ellipsoidal pores, said carbon foam having been derived from a pitch selected from the group consisting of synthetic mesophase pitch, synthetic isotropic pitch, petroleum-derived mesophase pitch, petroleum-derived isotropic pitch, and coal-tar-derived mesophase pitch.
A graphitic carbon foam having a specific thermal conductivity of at least 109 W·cm3/m·K·g, said carbon foam having an open cell pore structure comprised of pores whose planar cross sectional images are circular or elliptical, said carbon foam having been derived from a pitch selected from the group consisting of synthetic mesophase pitch, synthetic isotropic pitch, petroleum-derived mesophase pitch, petroleum-derived isotropic pitch, and coal-tar-derived mesophase pitch.
A graphitic carbon foam having a specific thermal conductivity of at least 109 W·cm3/m·K·g, wherein the carbon foam is a non-oxidatively stabilized carbon foam of an open cell structure comprising cell walls wherein carbon in the form of graphite and derived from a mesophase pitch is aligned along the cell wall axes.
A graphitic carbon foam characterized by a specific thermal conductivity greater than four times that of copper and an x-ray diffraction pattern as depicted in FIG. 11, said foam being pitch-derived, non-oxidatively stabilized, and further characterized by an open cell pore structure comprised of ellipsoidal pores and by graphite aligned along the axes of the cell walls.
A graphitic carbon foam further characterized by a specific thermal conductivity greater than four times that of copper and an x-ray diffraction pattern as depicted in FIG. 11, said foam being mesophase pitch-derived, non-oxidatively stabilized and characterized (1) by an open cell pore structure consisting essentially of pores whose planar cross sectional images are circular or elliptical and (2) by carbon aligned along the axes of the cell walls.
Dependencies are inferred from the claim text.