Process and product for lubricating metal prior to cold forming

A composition for lubricating a metal workpiece prior to cold forming, the composition consisting essentially of:

• at least one aqueous alkaline stearate compound adapted to, and present in an amount sufficient to impart metal lubrication between about 180° F. and about 320° F.;
• at least one aqueous alkaline palmitate compound adapted to, and present in an amount sufficient to impart metal lubrication below about 160° F.;
• at least one aqueous metallic stearate compound adapted to, and present in an amount sufficient to impart metal lubrication between about 240° F. and 320° F.;
• at least one polymeric glycol adapted to, and present in an amount sufficient to provide temperature stability, act as a carrier for the aqueous compounds, and impart a waxy lubrication to the metal;
• at least one hydrotropic agent adapted to, and present in an amount sufficient to solubilize the lubricating composition;
• and
• at least one stabilizing agent adapted to, and present in an amount sufficient to maintain solution stability among soluble constituents and to provide dispersing and suspending action among insoluble constituents, wherein the at least one stabilizing agent is from the chemical family of naphthalene sulfonic acids.

A composition for lubricating a metal workpiece prior to cold forming, the composition consisting essentially of:

• at least one aqueous alkaline stearate compound adapted to, and present in an amount sufficient to impart metal lubrication between about 180° F. and about 320° F.;
• at least one aqueous alkaline palmitate compound adapted to, and present in an amount sufficient to impart metal lubrication below about 160° F.;
• at least one aqueous metallic stearate compound adapted to, and present in an amount sufficient to impart metal lubrication between about 240° F. and 320° F.;
• at least one polymeric glycol adapted to, and present in an amount sufficient to provide temperature stability, act as a carrier for the aqueous compounds, and impart a waxy lubrication to the metal;
• at least one hydrotropic agent adapted to, and present in an amount sufficient to solubilize the lubricating composition;
• at least one stabilizing agent adapted to, and present in an amount sufficient to maintain solution stability among soluble constituents and to provide dispersing and suspending action among insoluble constituents;
• and
• a de-foaming agent adapted to, and present in an amount sufficient to lay at the surface of the lubricating composition to break up soap bubbles as they form and to prevent foam and froth.

A process for lubricating a metal workpiece outer surface prior to cold forming, the process comprising the step of:

• disposing a non-reactive lubricating composition on the workpiece outer surface, the outer surface having been cleaned and rinsed, the lubricating composition consisting essentially of:
• at least one aqueous alkaline stearate compound adapted to, and present in an amount sufficient to impart metal lubrication between about 180° F. and about 320° F.;
• at least one aqueous alkaline palmitate compound adapted to, and present in an amount sufficient to impart metal lubrication below about 160° F.;
• at least one aqueous metallic stearate compound adapted to, and present in an amount sufficient to impart metal lubrication between about 240° F. and 320° F.;
• at least one polymeric glycol adapted to, and present in an amount sufficient to provide temperature stability, act as a carrier for the aqueous compounds, and impart a waxy lubrication to the metal;
• at least one hydrotropic agent adapted to, and present in an amount sufficient to solubilize the lubricating composition;
• and
• at least one stabilizing agent adapted to, and present in an amount sufficient to maintain solution stability among soluble constituents and to provide dispersing and suspending action among insoluble constituents, wherein the at least one stabilizing agent is from the chemical family of naphthalene sulfonic acids.

A process for lubricating a metal workpiece outer surface prior to cold forming, the process comprising the step of:

• disposing a non-reactive lubricating composition on the workpiece outer surface, the outer surface having been cleaned and rinsed, the lubricating composition consisting essentially of:
• at least one aqueous alkaline stearate compound adapted to, and present in an amount sufficient to impart metal lubrication between about 180° F. and about 320° F.;
• at least one aqueous alkaline palmitate compound adapted to, and present in an amount sufficient to impart metal lubrication below about 160° F.;
• at least one aqueous metallic stearate compound adapted to, and present in an amount sufficient to impart metal lubrication between about 240° F. and 320° F.;
• at least one polymeric glycol adapted to, and present in an amount sufficient to provide temperature stability, act as a carrier for the aqueous compounds, and impart a waxy lubrication to the metal;
• at least one hydrotropic agent adapted to, and present in an amount sufficient to solubilize the lubricating composition;
• and
• at least one stabilizing agent adapted to, and present in an amount sufficient to maintain solution stability among soluble constituents and to provide dispersing and suspending action among insoluble constituents;
• wherein before the lubricating composition is disposed on the workpiece outer surface, the process further comprises the step of applying an organic conversion coating composition to the surface, and wherein the coating composition consists essentially of:
• at least one glucose derivative present in an amount sufficient to form a loose, soft and pliable layer of powdery crystals;
• at least one meta-phosphate compound present in an amount sufficient to provide linkage from the organic layer to the metal surface;
• and
• a source of nitrate/nitrite in the form of metallic or alkali earth compounds, in an amount sufficient to provide limited acceleration for the organic deposit.

A process for lubricating a metal workpiece outer surface prior to cold forming, the process comprising the step of:

• disposing a non-reactive lubricating composition on the workpiece outer surface, the outer surface having been cleaned and rinsed, the lubricating composition consisting essentially of:
• at least one aqueous alkaline stearate compound adapted to, and present in an amount sufficient to impart metal lubrication between about 180° F. and about 320° F.;
• at least one aqueous alkaline palmitate compound adapted to, and present in an amount sufficient to impart metal lubrication below about 160° F.;
• at least one aqueous metallic stearate compound adapted to, and present in an amount sufficient to impart metal lubrication between about 240° F. and 320° F.;
• at least one polymeric glycol adapted to, and present in an amount sufficient to provide temperature stability, act as a carrier for the aqueous compounds, and impart a waxy lubrication to the metal;
• at least one hydrotropic agent adapted to, and present in an amount sufficient to solubilize the lubricating composition;
• and
• at least one stabilizing agent adapted to, and present in an amount sufficient to maintain solution stability among soluble constituents and to provide dispersing and suspending action among insoluble constituents;
• wherein simultaneous with the lubricating composition being disposed on the workpiece outer surface, the process further comprises the step of applying an organic conversion coating composition to the surface, and wherein the coating composition consists essentially of:
• at least one glucose derivative present in an amount sufficient to form a loose, soft and pliable layer of powdery crystals;
• at least one meta-phosphate compound present in an amount sufficient to provide linkage from the organic layer to the metal surface;
• and
• a source of nitrate/nitrite in the form of metallic or alkali earth compounds, in an amount sufficient to provide limited acceleration for the organic deposit.

A composition for depositing an organic conversion coating on a metal workpiece prior to or simultaneous with lubrication and prior to cold forming, the coating composition consisting essentially of:

• at least one glucose derivative present in an amount sufficient to form a loose, soft and pliable layer of powdery crystals, wherein the glucose derivative is dextrose and is present in an amount ranging between about 70 grams/liter to about 125 grams/Liter;
• at least one meta-phosphate compound present in an amount sufficient to provide linkage from the organic layer to the metal surface, wherein the meta-phosphate compound is sodium hexa-meta phosphate and is present in an amount ranging from about 60 grams/liter to about 140 grams/liter;
• and
• a source of nitrate/nitrite in the form of metallic or alkali earth compounds, in an amount sufficient to provide limited acceleration for the organic deposit, wherein the source of nitrate/nitrite is sodium nitrate and is present in an amount ranging from about 12 grams/liter to about 32 grams/liter.

A composition for lubricating a metal workpiece prior to cold forming, the composition consisting of:

• at least one aqueous alkaline stearate compound adapted to, and present in an amount sufficient to impart metal lubrication between about 180° F. and about 320° F.;
• at least one aqueous alkaline palmitate compound adapted to, and present in an amount sufficient to impart metal lubrication below about 160° F.;
• at least one aqueous alkaline stearate compound adapted to, and present in an amount sufficient to impart metal lubrication between about 240° F. and 320° F.;
• at least one polymeric glycol adapted to, and present in an amount sufficient to provide temperature stability, act as a carrier for the aqueous compounds, and impart a waxy lubrication to the metal;
• at least one hydrotropic agent adapted to, and present in an amount sufficient to solubilize the lubricating composition;
• at least one stabilizing agent adapted to, and present in an amount sufficient to maintain solution stability among soluble constituents and to provide dispersing and suspending action among insoluble constituents;
• and
• a dispersing agent/polyelectrolyte for maintaining the aqueous compounds in solution and for imparting a cohesive film strength to the lubricating composition as it is dried on the metal workpiece.