Inhomogenous composite doped film for low temperature reflow

Abstract

Lower reflow temperature in dielectrics is obtained by using a composite dielectric film. The composite dielectric film includes a first layer doped in the conventional range. A borophosphosilicate glass (BPSG) thick layer having concentrations of around 4.4 wt. % boron and around 5.6 wt. % phosphorus is exemplary. The composite dielectric film includes a second layer doped excessively. A BPSG thin layer having concentrations between 1-4 wt. % phosphorus and between 7-8 wt. % boron is exemplary. A capping layer of conventional dopant concentration may be additionally added to prevent outdiffusion. A composite dielectric BPSG film can be reflowed around 700° C. as compared to the typical 800-900° C. range. After reflow, etching away the second highly doped layer removes any potential adverse effects.