Synthesis of SAPO-44
AssigneeExxon Mobil Chemical Patents Inc.
InventorsZhongmin Liu, Xiexian Guo, Guangyu Cai
Life of this patent
Estimating the term…
Abstract
A method for making molecular sieves comprising silicoaluminophosphate 44 (SAPO-44) or substantially pure SAPO-44 and a method for using the molecular sieves so prepared for oxygenate conversion to olefins.
Claims10
A SAPO-44 molecular sieve, wherein said SAPO-44 comprises 30.9 to 61.0 percent Si(4Al) species.
A SAPO-44 molecular sieve which is made by a method comprising:
- forming a mixture comprising, a silicon component, an aluminum component, an organic template at a ratio of organic template to aluminum of at least 1, and a phosphorus component;
- and
- subjecting said mixture to conditions effective to produce said SAPO-44 , wherein the SAPO-44 contains 30.9 to 61.0 percent Si(4Al) species.
A SAPO-44 molecular sieve made by a method comprising:
- forming a mixture comprising, a silicon component, an aluminum component, a phosphorus component, and an organic template, said mixture having the formula TaSiwAlxPyOz·b H2O, excluding other species present in said mixture, wherein T represents the organic template, a/w is from about 2 to about 8, a/x is from about 1 to about 5, a/y is from about 1 to about 5, y/x is from about 1 to about 0.2, and a/b is from about 0.02 to about 0.2;
- and
- subjecting said mixture to conditions effective to produce said SAPO-44, wherein said SAPO-44 contains 30.9 to 61.0 percent Si(4Al) species.
A SAPO-44 molecular sieve composition made by a method comprising:
- mixing boehmite with an aqueous orthophosphoric acid solution under first condition effective to form a first product;
- adding a silica gel to said first product under second conditions effective to form a second product;
- adding a mixture comprising cyclohexylamine and water to said second product under third conditions effective to form a third product wherein said third product exhibits a pH from about 5.5 to about 8.5 and comprises a compound of the formula TaSiwAlxPyOz·b H2O, wherein T represents cyclohexylamine, a/w is from about 2 to about 8, a/x is from about 1 to about 5, a/y is from about 1 to about 5, y/x is from about 1 to about 0.2, and a/b is from about 0.02 to about 0.2;
- subjecting said third product to a temperature in the range of from about 100° C. to about 270° C. for a period of time sufficient to form a solid material;
- drying said solid material at a temperature from about 25° C. to about 120° C. and at a pressure from about 0.01 kPa to about 150 kPa to form a dried solid material;
- and
- calcining said dried solid material to form said SAPO-44 molecular sieve composition, wherein said SAPO-44 has 30.9 to 61.0 percent Si(4Al) species.
A SAPO-44 molecular sieve made from a reaction mixture having the formula TaSiwAlxPyOz·b H2O, wherein T represents an organic template, a/w is from about 2 to about 8, a/x is from about 1 to about 5, a/y is from about 1 to about 5, y/x is from about 1 to about 0.2, and a/b is from about 0.02 to about 0.2, wherein said SAPO-44 contains 30.9 to 61.0 percent Si(4Al) species.