Coating for optical discs

#This invention relates to the process for the manufacturing of optical data storing surfaces, in particular compact discs. It further relates to providing a removable protective coating on the surfaces of the discs during manufacturing.

#Plastic discs having a pit optical track structure are well known as compact discs. The term compact disc as used in this application includes any disc shaped recorded medium having pits and lands forming an optical track structure on a data information recording planar surface. Thus it includes such discs where the information stored as pits and lands is digital information, analog information, or information of a graphic or holographic nature. Examples of the different types of information storage are as follows: Digital information may be encoded into the pits and lands as pits of quantized lengths interpretable as a stream of digital data, wherein the length of each pit or land segment may be, for example, related to the number of 1's or 0's in a data stream. An example of such a system is the compact disc (“CD”) audio or video disc. Analog information may be encoded into the pits and lands as pit lengths that may vary over a continuum of values, wherein the length of each pit or land segment may be, for example, related to a voltage level in a desired output. An example of such a system is the laser disc video recording system. Graphics may be placed on the surface of a disc by employing the light reflection properties of pitted surfaces that are visible to the unaided eye. Similarly holographic information may be stored in a pit/land format, particularly where it is possible to vary the pit depth to create reflection interference patterns that are visible as a holographic image viewable by the unaided eye.

#In-line manufacturing systems are utilized for mass producing copies of compact discs. These systems are capable of producing a compact disc every few seconds once a master disc has been produced. The process employs injection molding, electroplating and printing stages.

#FIG. 1 depicts a side view of the present invention.

#FIG. 2 depicts a top view of the present invention with the protective layer partly pealed back.

#It is desired in accordance with the object of the invention to adhere temporarily a material, preferably such as ethylene vinyl acetate (EVA), to the surface of the disc that must be protected from dust, etc. The application method is designed to operate on an assembly line. A roll of a matrix of the protective film passes between an applicator and a line along which the discs to be protected are being fed. The protective film applicator may be a flat plate which moves to engage the protective coating film and bring it into contact with the disc. The applicator may either cut the appropriate shape from the matrix of materials or pick a precut shape from the matrix.

#In order to facilitate the application of the protective substrate and its adhesive by automated methods the substrate cannot be too thin or subject to tearing. The preferred embodiment is to use material for the substrate in a modulus range B>5,000 p.s.i, ASTM D790 73F. To be scratch resistant the thickness is preferred to be greater than 5 microns and the hardness greater than Shore D 10. The substrate also must not be subject to shrinkage that could distort the disc. Preferably the shrinkage is less than 8% at 70 C for 96 hours.

#With regard to the characteristics of the adhesive, it must be able to be removed easily and without residue. In the preferred embodiment is a vinyl acetate adhesive for which the peel off pressure is less than 0.01 p.s.i. and no residues of the adhesive are greater than 10 microns in any dimension.