Polymer blend compositions based on isotactic polypropylene homopolymer and injected molded articles thereof

A polypropylene-based resin composition comprising:

• (1) 95 to 50% by weight of a polypropylene-based resin (A) composed of the following (i) and (ii);
• (i) a crystalline polypropylene composition obtained by polymerizing propylene in the presence of a stereoregular polymerization catalyst thereby to produce a crystalline propylene homopolymer as a first segment, and subsequently copolymerizing ethylene and propylene to produce a propylene-ethylene random copolymer as a second segment, said crystalline polypropylene composition having a melt flow rate (MFR) at 230° C. measured according to JIS-K-6758 of not less than 25 g/10 min., wherein the first segment (i) has a Q value of from 3.0 to 5.0, and an isotactic pentad fraction of not less than 0.97, the second segment has an ethylene content of from 25 to 55% by weight and an intrinsic viscosity (η)EP of from 3.0 to 6.0 dl/g, and
• (ii) a crystalline propylene homopolymer having a melt flow rate at 230° C. measured according to JIS-K-6758 of not less than 70 g/10 min., the crystalline propylene homopolymer (ii) has a Q value of from 3.0 to 5.0 and an isotactic pentad fraction of not less than 0.97;
• (2) 5 to 20% by weight of a rubber (B) selected from the group consisting of an ethylene-α-olefin copolymer rubber (a) selected from the group consisting of an ethylene-1-hexene copolymer rubber and ethylene-1-octene copolymer rubber, and a mixture of an alkenyl aromatic compound-containing rubber (b) with the ethylene-α-olefin copolymer (a), wherein the rubber (a) is an ethylene-α-olefin copolymer rubber having a melt flow index measured at 190° C. under a load of 2.16 kg according to JIS K6758 of 0.5 to 10 g/10 min.;
• and
• (3) 0 to 30% by weight of talc (C) having an average particle diameter of not more than 3 μm, the total amount of (A), (B) and (C) being 100% by weight, wherein said polypropylene-based resin composition satisfies the following expression:
• 0.05≦((A)′/((A)′+(a′)+(b′)))≦0.20,
• wherein (A)′ represents an amount by weight of the propylene random copolymer as the second segment of the (i) in the polypropylene-based resin composition, (a′) represents an amount by weight of the ethylene-α-olefin copolymer rubber (a) in the polypropylene-based resin composition, and (b′) represents an amount by weight of the alkenyl aromatic compound-containing rubber in the polypropylene-based resin composition, and
• wherein the melt flow rate at 230° C. measured according to JIS-K-6758 of said polypropylene-based resin composition is not less than 35 g/10 min. and the flexural modulus at 23° C. is not less than 8000 kg/cm2.