Hydrotalcite compounds of low uranium (U) content and processes for their preparation
AssigneeKyowa Chemical Industry Co., Ltd.
InventorsAkira Okada, Satoko Yamashita, Koji Shimizu
Life of this patent
Estimating the term…
Abstract
Hydrotalcite compounds useful as additives to synthetic resins such as epoxy resins which are used as, in particular, sealant for semiconductor devices such as transister, IC, LSI and the like, which are characterized by having a composition represented by the formula (1) below: M1−X2+AlX3+(OH)2A2−X/2·mH2O (1) in which M2+ is at least one of Mg2+ and Zn2+, x is a positive number in the range of 0.2≦x≦0.5, A2− is at least one of CO32− and SO42−, and m is a number in the range of 0-2, and having a uranium (U) content of not more than 10 ppb, an average secondary particle size of not more than about 3 μm and a BET specific surface area of not more than 30 m2/g.
Claims6
A process for producing a hydrotalcite compound derived from a water-soluble magnesium compound and a water-soluble aluminium compound which contain(s) at least 50 ng/g (ppb) of a uranium compound as calculated in terms of uranium (U) based on Mg(OH)2 and/or Al(OH)3, said hydrotalcite compounds being represented by the formula (1) below:
- Mg1−X2+AlX3+(OH)2AX/22−·mH2O (1)
- in which
- x is a positive number in the range of 0.2≦x≦0.5,
- A2− is at least one of CO32− and SO42−, and
- m is a number in the range of 0-2, having an average secondary particle size of not more than 3 μm and a BET specific surface area of not more than 30 m2/g and wherein they have a uranium (U) content of not more than 10 ppb,
- which comprises
- (1) subjecting an aqueous solution of the water-soluble aluminium compound and the water-soluble magnesium compound, which as a whole contain a uranium compound in an amount corresponding to at least 50 ng of uranium (U) as calculated per gram of Mg(OH)2 and/or Al(OH)3, to a coprecipitation reaction under alkaline conditions, the composition of the starting materials satisfying the molar ratio within the range defined by the formula (2) below:
- 0.15 ≦ at least one of CO 3 2 - and SO 4 2 - Mg 2 + + Al 3 + ≦ 1.25 , ( 2 )
- at temperatures of 10-50° C. under stirring, and
- (2) subjecting the resulting coprecipitation product, without isolating it from the suspension which served as the mother liquor of the coprecipitation reaction, to a hydrothermal reaction at a temperature of 90-200° C. for at least 0.5 hour, while keeping the pH of the reaction suspension within the range of 7.0-13.5.
A process for producing hydrotalcite compounds that are represented by the formula 1:
- M 1 - X 2 + Al X 3 + ( OH ) 2 A X / 2 2 - · mH 2 O ( 1 )
- in which
- M2+ is at least one of Mg2+ and Zn2+,
- x is a positive number in the range of 0.2≦x≦0.5,
- A2− is at least one of CO32− and SO42−, and
- m is a number in the range of 0-2, and have a uranium (U) content of not more than 10 ppb, an average secondary particle size of not more than about 3 μm and a BET specific surface area of not more than 30 m2/g,
- which comprises
- (1) subjecting an aqueous solution of water-soluble aluminium compound and an aqueous solution of water-soluble magnesium compound and/or water-soluble zinc compound to a coprecipitation reaction under alkaline conditions, the composition of the starting materials satisfying the molar ratio within the range defined by the formula (2) below:
- 0.15 ≦ at least one of CO 3 2 - and SO 4 2 - M 2 + + Al 3 + ≦ 1.25 ( 2 )
- in which M2+ stands for at least one of Mg2+ and Zn2+, at temperatures of 10-50° C. under stirring, and
- (2) subjecting the resulting coprecipitation product, without isolating it from the suspension which served as the mother liquor of the coprecipitation reaction, to a hydrothermal reaction at temperatures of 90-200° C. for at least 0.5 hour,
- (3) adjusting the reaction conditions in that occasion that the pH of the reaction suspension which has undergone the hydrothermal reaction should fall within the range of 7.0-13.5, and after carrying out the hydrothermal reaction,
- (4) suspending the hydrothermal reaction product, which has been washed with water, in an aqueous solution of ammonium carbonate and/or alkali carbonate or ammonium carbonate and/or alkali hydrogen carbonate, followed by 1-24 hours stirring at temperatures of 10-100° C.