# US 6,284,808 B1 · Inline solid state polymerization of PET flakes for manufacturing plastic strap by removing non-crystalline materials from recycled PET > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 6,284,808 B1 - Document ID: US6284808B1 - Status: Granted - Kind: B1 - Application number: 09/170,808 - Filed: 1998-10-13 - Granted: 2001-09-04 - Earliest claimed: 1997-02-03 - Assignees: Illinois Tool Works Inc. - Inventors: William Donald Robinson; Gary L. Vadnais - Web page: https://patentgrep.com/patent/US6284808B1 ## CPC - C08J 11/06: without chemical reactions - B29C 48/287: {Raw material pre-treatment while feeding (B29C48/78 takes precedence)} - C08G 63/80: Solid-state polycondensation - B29C 48/04: Particle-shaped (making granules B29B9/00) - C08J 2367/00: Characterised by the use of polyesters obtained by reactions forming a carboxylic ester link in the main chain; Derivatives of such polymers - C08J 2367/02: Polyesters derived from dicarboxylic acids and dihydroxy compounds; (C08J2367/06 takes precedence) - Y02W 30/62: Plastics recycling; Rubber recycling - C08J: WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H (working, e.g. shaping, of plastics B29) - B29C: SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING (making preforms B29B11/00; making laminated products by combining previously unconnected layers which become one product whose layers will remain together B32B37/00 - B32B41/00) - C08G: MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS - Y02W: CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO WASTEWATER TREATMENT OR WASTE MANAGEMENT ## Abstract A process for preparing a PET flake mixture for use in connection with the fabrication of high-performance plastic strapping comprises the steps of initially collecting post-consumer and non-post-consumer PET materials having an initially wide range of relatively low intrinsic viscosity (IV) values with a relatively low average intrinsic viscosity (IV) value, and processing the same through solid state polymerization (SSP) so as to obtain a wide range of relatively high intrinsic viscosity (IV) values with a relatively high average intrinsic viscosity (IV) value. The initially collected materials are chopped into flakes and chunks, and the chunks are removed by a suitable destoner so as to render the remaining mixture comprised substantially entirely of flake materials or segments. This is advantageous because the flake segments, as opposed to the chunk segments, are able to be substantially increased in intrinsic viscosity (IV) values and within a relatively short period of time, and in addition, the flake segments are essentially crystalline while the chunk segments are essentially non-crystalline which would otherwise undergo rapid crystallization and generate a substantial amount of heat of crystallization. Such heat of crystallization undesirably raises the temperature of the polymerization process whereby the materials tend to become sticky and agglomerate thereby impeding the flow of the materials being processed as well as tending to clog components of the processing apparatus. ## Claims ### Claim 1 A heterogeneous mixture of polyethylene terephthalate (PET) material mixture which is suitable for subsequent processing, comprising: a single batch mixture of heterogeneous PET material which has a relatively wide distribution of intrinsic viscosity (IV) values, which are primarily within the range of 0.60 to 0.80 dl/g, but as high as 0.90 dl/g, and wherein said single batch mixture has been derived from an initial mixture comprising substantially crystalline flake segments and substantially non-crystalline chunk segments from which said substantially non-crystalline chunk segments have been removed such that said mixture comprises substantially only said substantially crystalline flake segments, whereby when said heterogeneous mixture of said PET materials comprising substantially only said substantially crystalline flake segments is processed further so as to increase said intrinsic viscosity (IV) values of said PET materials, the generation of a substantial amount of heat of crystallization within said processed mixture of said PET materials will be effectively prevented. ### Claim 2 (depends on 1) A mixture as set forth in claim 1, wherein: said further processed PET materials have an intrinsic viscosity (IV) value range of 0,90 dl/g to 1.5 dl/g. ### Claim 3 A heterogeneous solid stated polyethylene terephthalate (PET) material for use in making high-performance strapping, comprising: a single batch mixture of heterogeneous PET material which has a relatively wide distribution of intrinsic viscosity (IV) values, which are primarily within the range of 0.60 to 0.80 dl/g, but as high as 0.90 dl/g, wherein said single batch mixture has been derived from an initial mixture comprising substantially crystalline flake segments and substantially non-crystalline chunk segments from which said substantially non-crystalline chunk segments have been removed such that said mixture comprises substantially only said substantially crystalline flake segments, and wherein said single batch mixture has been solid stated directly while in said heterogeneous mixture state so as to increase said intrinsic viscosity (IV) values of said PET materials without generating a substantial amount of heat of crystallization. ### Claim 4 (depends on 3) A heterogeneous solid stated polyethylene terephthalate (PET) materials as set forth in claim 3, wherein: said solid stated PET material has an intrinsic viscosity (IV) value range of 0.90 dl/g to 1.5 dl/g. ### Claim 5 A high performance plastic strap, comprising: a polyethylene terephthalate (PET) material which has been solid stated directly from a single batch heterogeneous mixture of PET material which has a relatively wide distribution of intrinsic viscosity (IV) values, which are primarily within the range of 0.60 to 0.80 dl/g, but as high as 0.90 dl/g, and wherein said single batch heterogeneous mixture has been derived from an initial mixture comprising substantially crystalline flake segments and substantially non-crystalline chunk segments from which said substantially non-crystalline chunk segments have been removed such that said said initial mixture comprises substantially only said substantially crystalline flake segments so as to increase said intrinsic viscosity (IV) values of said PET materials without generating a substantially amount of heat of crystallization. ### Claim 6 (depends on 5) A high-performance plastic strap as set forth in claim 5, wherein: said solid stated polyethylene terephthalate (PET) material has an intrinsic viscosity (IV) value range of 0.90 dl/g to 1.5 dl/g.