Refractory compositions
AssigneeFoseco International Limited
InventorsGerd Trinkl, Manfred Fessel, Vincent Edward Mellows, Reinhard Stötzel
Life of this patent
Estimating the term…
Abstract
Substantially dry, self-hardening, thermally activated refractory compositions, suitable for use to produce linings for furnaces or metallurgical vessels such as ladles, tundishes or launders, comprise particulate refractory material, an inorganic binder having associated therewith chemically or physically bound water such as sodium metasilicate pentahydrate or tribasic sodium phosphate dodecahydrate, and an element or compound, such as aluminium, which will react exothermically with the inorganic binder. The compositions may also contain an inhibitor such as a mineral oil or a vegetable oil to inhibit premature exothermic reaction.
Claims8
A substantially dry, self-hardening, thermally activated refractory composition comprising a particulate refractory material, an inorganic binder having chemically or physically bound water associated therewith and an element or compound which will react exothermically with the inorganic binder, characterized in that the composition contains 70% to 95% by weight of particulate refractory material, 1% to 15% by weight of the inorganic binder, including the chemically or physically bound water and 1% to 15% by weight of the element or compound which will react exothermically with the inorganic binder;
- and wherein the inorganic binder has physically bound water associated therewith and comprises micro-encapsulated sodium silicate solution or micro-encapsulated aqueous aluminum orthophosphate solution.
A substantially dry, self-hardening, thermally activated refractory composition comprising a particulate refractory material, an inorganic binder having chemically or physically bound water associated therewith and an element or compound which will react exothermically with the inorganic binder, characterized in that the composition contains 70% to 95% by weight of particulate refractory material, 1% to 15% by weight of the inorganic binder including the chemically or physically bound water, and 1% to 15% by weight of the element or compound which will react exothermically with the inorganic binder;
- and wherein the composition also contains a mineral oil or a vegetable oil.
A substantially dry, self-hardening, thermally activated refractory composition comprising:
- a particulate refractory material in the amount of between 70-95% by weight;
- an inorganic binder having chemically or physically bound water associated therewith in the amount of 1-15% by weight;
- and
- an element or compound which will react exothermically with the inorganic binder, said element or compound in the amount of 1-15% by weight, and said element or compound comprising calcium oxide, magnesium oxide, or aluminum;
- said refractory material held by said inorganic binder after exothermic reaction with said element or compound so as to provide a substantially dry, self-hardened, thermally activated refractory composition.
A substantially dry, self-hardening, thermally activated refractory composition comprising:
- a particulate refractory material in the amount of between 70-95% by weight;
- a binder, said binder consisting essentially of an inorganic binder having chemically or physically bound water associated therewith in the amount of 1-15% by weight;
- and
- an element or compound which will react exothermically with the inorganic binder, said element or compound in the amount of 1-15% by weight, said element or compound being aluminum, calcium oxide, or magnesium oxide;
- said refractory material held by said inorganic binder after exothermic reaction with said element or compound so as to provide a substantially dry, self-hardened, thermally activated refractory composition.
A substantially dry, self-hardening, thermally activated refractory composition comprising:
- a particulate refractory material in the amount of between 70-95% by weight, and wherein said particulate refractory material is silica, zircon, silicon carbide, alumina, magnesia, calcined dolomite, chrome magnesite, olivine, forsterite, mullite, kyanite, andalusite, chamotte, carbon, or chromite, or a mixture of two or more of those materials;
- a binder, said binder consisting essentially of an inorganic binder having chemically or physically bound water associated therewith in the amount of 1-15% by weight, and wherein the inorganic binder has chemically bound water associated therewith, and comprises a crystalline hydrated salt selected from the group consisting of silicates, carbonates, sulphates, nitrates, borates and phosphates;
- an element or compound which will react exothermically with the inorganic binder, said element or compound in the amount of 1-15% by weight;
- said refractory material held by said inorganic binder after exothermic reaction with said element or compound so as to provide a substantially dry, self-hardened, thermally activated refractory composition;
- and
- a mineral oil or vegetable oil in an amount of 0.1-5% by weight.