In a method of resin-encapsulating a semiconductor chip using a polytetrafluoroethylene film as the mold-releasing film, a polytetrafluoroethylene film F wherein the thermal shrinkage percentages thereof in both the longitudinal direction and the width direction are 5% or lower, the difference of the thermal shrinkage percentages is within 3%, and the ratio of the elastic modulus of the longitudinal direction to the elastic modulus of the width direction is from 0.5 to 2.0 during resin encapsulating is used. By using the mold-releasing film, resin encapsulating can be carried out with an excellent yield while preventing the occurrence of resin covering of the terminals or the top surfaces of the post electrodes.
A method of resin-encapsulating a semiconductor chip by closing a lower mold having disposed in a cavity thereof a semiconductor chip equipped with terminals or post electrodes by an upper mold via a mold-releasing film made of a polytetrafluoroethylene film between the surface on which the terminals or the post electrodes are disposed and the upper mold and then injecting a resin into the cavity of the lower mold and cured, the polytetrafluoroethylene film satisfying the conditions that the thermal shrinkage percentages in the longitudinal and width directions are 5% or lower, the difference between the thermal shrinkage percentages is within 3%, and the ratio of the elastic modulus of the longitudinal direction to the elastic modulus of the width direction is from 0.5 to 2.0 during resin encapsulating.
A mold-releasing film used for a method of resin-encapsulating a semiconductor chip, wherein the mold-releasing film is made of a polytetrafluoroethylene film which satisfies the conditions that the thermal shrinkage percentages in the longitudinal and width directions at 175° C. for 10 minutes are 5% or lower, the difference between the thermal shrinkage percentages is within 3%, and the ratio of the elastic modulus of the longitudinal direction to the elastic modulus of the width direction is from 0.5 to 2.0 during resin encapsulating.
Dependencies are inferred from the claim text.