Method of producing an integrated circuit chip using low “k” factor hybrid photoresist and apparatus formed thereby

A method of producing an integrated circuit chip comprising the formation of a resist pattern which includes the steps of:

• selecting an enhanced resist composition having;
• a positive tone photoresist material partially protected with acid labile moieties as protective groups, wherein the degree of protection is sufficient to render the composition initially insoluble in aqueous base and may be de-blocked to increase solubility;
• wherein the acid labile moieties comprise acetals, ketals, or acrvlates;
• a cross-linker, having negative tone chemistry;
• wherein the composition is initially insoluble in aqueous base;
• wherein the amount of cross-linker compared to the degree of protection is less than the amount required to keep the composition insoluble in aqueous base after the single excitation event;
• and
• wherein the composition is rendered aqueous base soluble after the single excitation event even though the solubility of the exposed composition is reduced by the cross-linker response;
• depositing a layer of the selected positive photoresist material onto the substrate;
• exposing selected portions of the positive photoresist layer to light, wherein the exposed portions are soluble in aqueous base;
• and developing the exposed portions, wherein the exposed portions are removed.

A method for forming a resist pattern on a substrate comprising the steps of:

• selecting an enhanced negative photoresist composition having;
• one or more positive tone photoresist materials partially protected with acid labile moieties as protective groups, wherein the degree of protection is insufficient to render the composition initially insoluble in aqueous base and may be de-blocked to increase solubility;
• a cross-linker, having negative tone chemistry;
• wherein the composition is initially soluble in aqueous base;
• wherein the degree of protection compared to the amount of cross-linker is less than the amount required to keep the composition soluble in aqueous base after cross-linking occurs;
• and
• wherein the composition is rendered aqueous base insoluble after the single excitation event even though the solubility of the exposed composition is increased by de-blocking group response;
• depositing a layer of the selected negative photoresist material onto the substrate;
• exposing selected portions of the negative photoresist layer, wherein the exposed portions are insoluble in aqueous base;
• and
• developing the unexposed portions thereby removing the unexposed portions.

A method of producing an integrated circuit chip including the formation of a resist pattern comprising the steps of:

• selecting an enhanced negative photoresist composition having;
• one or more positive tone photoresist materials partially protected with acid labile moieties as protective groups, wherein the degree of protection is insufficient to render the composition initially insoluble in aqueous base and may be de-blocked to increase solubility;
• a cross-linker;
• wherein the composition is initially soluble in aqueous base;
• wherein the degree of protection compared to the amount of cross-linker is less than the amount required to keep the composition soluble in aqueous base after cross-linking occurs;
• and wherein the composition is rendered aqueous base insoluble after the single excitation event even though the solubility of the exposed composition is increased by de-blocking group response;
• depositing a layer of the selected photoresist material onto the substrate;
• exposing selected portions of the negative photoresist layer, wherein the exposed portions are insoluble in aqueous base;
• and
• developing the unexposed portions thereby removing the unexposed portions.