Superalloys with improved weldability for high temperature applications
AssigneeSiemens Westinghouse Power Corporation
InventorsBrij B. Seth, Easo P. George, Sudarsanum S. Babu, Gene M. Goodwin, Stanislaus A. David, Carol E. Moyer
Life of this patent
Estimating the term…
Abstract
A cast nickel-base superalloy component (10) is made having a composition containing small amounts of both boron and zirconium which are effective in combination to provide increased weldability, where such alloy is adapted for welding by weld (18) to a second superalloy piece, where the two pieces are firmly bonded together and have a Sigmajig transverse stress value (16) greater than 137.9 million Newtons per square meter.
Claims10
A high temperature resistant nickel base superalloy composition containing small amounts of both boron and zirconium which are effective in combination to provide increased weldability, where the range of boron in the composition is from 0.001 wt % to 0.005 wt. % and the range of zirconium is from 0.005 wt % to 0.05 wt %, and where Zr+B is from 0.011 wt % to 0.06 wt %, also containing, by weight percent:
- 20.0%-25% Cr;
- up to 19.5% Co;
- 3.4%-4.0% Ti;
- 1.6%-2.2% Al;
- where Al+Ti is from 5.0%-6.2%, with the balance substantially Ni.
A cast, high temperature resistant, creep resistant, nickel-base superalloy consisting essentially of the composition by weight percent:
- 20.0%-25.0% Cr;
- up to 19.5% Co;
- 3.4%-4.0% Ti;
- 1.6%-2.2% Al;
- 1.6%-2.4% W;
- 1.2%-1.6% Ta;
- 0.8%-1.2% Nb;
- 0.005%-0.08% Zr;
- 0.001%-0.005% B;
- where Al+Ti is from 5.0%-6.2% and Zr+B is from 0.005% to 0.06% with the balance Ni.
Dependencies are inferred from the claim text.