Process for applying polymer particles on substrate and coatings resulting therefrom
AssigneeE. I. Du Pont de Nemours and Company
InventorsBasil Volodymyr Gregorovich, George Kevork Kodokian
Life of this patent
Estimating the term…
Abstract
A heated substrate is dipped into a fluidized bed containing particles of polymer to coat the substrate. The coating can subsequently be leveled (and cured if thermosetting) by heating the coated substrate above the melting point of the polymer. The process can be employed to provide desirable properties such as corrosion resistance and aesthetic qualities to the substrate, and to apply very thin coatings.
Claims21
An improved process for coating a substrate with a polymer comprising heating said substrate, immersing said heated substrate into a fluidized bed of particles of the polymer, coating the substrate with the polymer and removing the coated substrate from the fluidized bed;
- wherein the improvement comprises:
- i) heating the substrate during said heating step to a temperature sufficient to tackify the polymer particles upon contact;
- ii) maintaining particle temperature in the fluidized bed below that at which the particles tackify;
- iii) covering substantially uniformly all surfaces of the heated substrate;
- iv) optionally heating the coated substrate to level the coating and to cure the polymer if it is thermosetting;
- and
- v) controlling the coating thickness, per unit time, to obtain thin coatings of up to 150 micrometers, by heating the substrate such that the coating temperature is within the tack temperature gradient but below Tm and maintaining particle sizes so that at least 80 weight percent are between 10 to 80 micrometers.
An improved process for coating a substrate with a polymer comprising heating said substrate, immersing said heated substrate into a fluidized bed of particles of the polymer, coating the substrate with the polymer and removing the coated substrate from the fluidized bed;
- wherein the improvement comprises:
- i) heating the substrate during said heating step to a temperature sufficient to tackify the polymer particles upon contact;
- ii) maintaining particle temperature in the fluidized bed below that at which the particles tackify;
- iii) covering substantially uniformly all surfaces of the heated substrate;
- controlling the coating thickness, per unit time by:
- (a) heating the substrate within the tack temperature gradient but below Tm and by maintaining particle sizes of at least 80 weight percent of said polymer particles between 10 to 80 micrometers to obtain thin coatings of up to 150 micrometers;
- or
- (b) heating the substrate above the tack temperature gradient, maintaining particle sizes of at least 80 weight percent of said polymer particles above 80 micrometers, or both to obtain thicker coatings of between 150 to 300 micrometers.
A process for producing a thin coating of up to 150 micrometers of a polymer on a substrate comprising:
- heating the substrate to a temperature sufficient to tackify the polymer upon contact;
- immersing the heated substrate in a fluidized bed of particles of the polymer to substantially uniformly cover all surfaces of the substrate with the polymer particles, said particles being maintained below the temperature at which said particles tackify;
- and
- removing the coated substrate from the fluidized bed to produce said thin coating thereon, wherein thickness of said thin coating is controlled by maintaining the temperature of the substrate above the tack temperature gradient but below Tm of said polymer and by using at least 80 weight percent of the polymer particles having particle sizes in the range of 10 to 80 micrometers.
A process for controlling thickness of a coating of a polymer on a substrate to up to 150 micrometers, said process comprising:
- heating the substrate to a temperature above the tack temperature gradient but below Tm of said polymer;
- and
- immersing the heated substrate in a fluidized bed of particles of the polymer to substantially uniformly cover all surfaces of the substrate with the polymer particles;
- wherein at least 80 weight percent of the polymer particles are of particle sizes in the range of 10 to 80 micrometers and wherein said particles are maintained below the temperature at which said particles tackify.
A process for producing a thick coating of above 150 micrometers of a polymer on a substrate comprising:
- heating the substrate to a temperature sufficient to tackify the polymer upon contact;
- immersing the heated substrate in a fluidized bed of particles of the polymer to substantially uniformly cover all surfaces of the substrate with the polymer particles, said particles being maintained below the temperature at which said particles tackify;
- and
- removing the coated substrate from the fluidized bed to produce said thick coating thereon, wherein thickness of said thick coating is controlled by maintaining the temperature of the substrate above the tack temperature gradient, employing at least 80 weight percent of the polymer particles having particle sizes above 80 micrometers, or both.