Loading patent…
AssigneeKabushiki Kaisha Ohara
InventorsSusumu Uehara, Yasuo Ochi
Estimating the term…
There is provided a long-lasting phosphor having a base crystal of {dot over (a)}kermanite crystal structure consisting of R′ (where R′ is one or more elements selected from the group consisting of Ca, Sr and Ba), Mg, Si, O and N and comprising Eu as an activator and one or more co-activators such as Dy. The long-lasting phosphor is produced by sintering materials including strontium nitrate to grow the base crystal of {dot over (a)}kermanite crystal structure, or by changing a solution containing constituent elements or material in the state of suspension into fine particles of liquid by atomization and thereafter heating the fine particles of liquid in a gas stream under oxidating, neutral or reducing atmosphere. The new Mohs' scale of hardness of the long-lasting phosphor is less than 1. Phosphorescence brightness of the long-lasting phosphor 2 minutes after stoppage of irradiation of illuminance of 1000 lux for 30 minutes with a white fluorescent lamp is 200 mCd/m2 or over.
A long-lasting phosphor halving a base crystal comprising Eu as an activator and Ln as a co-activator where Ln is one or more elements selected from the group consisting of Sc, Y, La, Ce, Pr, Nd, Sm, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu and Bi, said base crystal having {dot over (a)}kermanite crystal structure consisting of R′ (where R′ is one or more elements selected from the group consisting of Ca, Sr and Ba), Mg, Si, O and N.
A powdered long-lasting phosphor having an average particle diameter within a range from 1.0 μm to 70 μm and a coefficient of variation of the particle diameter which is 100% or less, having a complex oxide type crystal as the base crystal and comprising an activator and a co-activator and being produced by changing a solution containing constituent elements or a mixture in the state of suspension into fine particles of liquid by atomization and thereafter heating the fine particles of liquid in a gas stream under an oxidating, neutral or reducing atmosphere.
A powdered long-lasting phosphor laving a complex oxide type crystal as the base crystal and comprising an activator and a co-activator, which is a compound having a chemical composition RO.aR′2O3.bR″2O3 (where R is one or more elements selected from the group consisting of Mg, Ca, Sr, Ba and Zn, R′ is Al or B, R″ is Y or Sc, and 0.5≦a≦3.0 and 0.001≦b≦0.02) and, as an activator, Eu in an amount within a range from 0.001% to 20% in mol % to the metal element or elements represented by R and, as a co-activator, one or more elements selected from the group consisting of Ce, Pr, Nd, Sm, Tb, Dy, Ho, Er, Tm, Yb and Lu in an amount within a range from 0.001% to 20% in mol % to the metal element or elements represented by R, and being produced by changing a solution containing constituent elements or a mixture in the state of suspension into fine particles of liquid by atomization and thereafter heating the fine particles of liquid in a gas stream tinder an oxidating, neutral or reducing atmosphere.
A powdered long-lasting phosphor having a complex oxide type crystal as the base crystal and comprising an activator, which is a compound having the chemical composition RO.aR′2O3.bR″2O3 (where R is one or more elements selected from the group consisting of Mg, Ca, Sr, Ba and Zn, R′ is Al or B, R″ is Y or Sc, and 0.5≦a≦3.0 and 0.001≦b≦0.02) and, as an activator, Eu in an amount within a range from 0.001% to 20% in mol % to the metal element or elements represented by R, and being produced by changing a solution containing constituent elements or a mixture in the state of suspension into fine particles of liquid by atomization and thereafter heating the fine particles of liquid in a gas stream under an oxidating, neutral or reducing atmosphere.
Dependencies are inferred from the claim text.