Reactive hot melt adhesive
AssigneeAshland Inc.
InventorsChung-Ying Chang, Gary J. Walsworth
Life of this patent
Estimating the term…
Abstract
The present invention relates to solvent free, moisture-curable, reactive hot melt adhesive compositions that are solid at room temperature, methods of making the compositions, and laminates prepared using the compostions. The compositions are a mixture comprising an isocyanate terminated prepolymer and a thermoplastic vinyl chloride copolymer.
Claims11
A solvent free, moisture-curable, hot melt adhesive composition which is solid at room temperature, consisting essentially of a mixture of;
- (a) an isocyanate terminated prepolymer with an isocyanate index greater than about 2, comprising the reaction product of an aliphatic polyester polyol or mixture of aliphatic polyester polyols and a polyisocyanate or mixture of polyisocyanates, and
- (b) a thermoplastic copolymer having a weight average molecular weight greater than 30,000 which is compatible with the isocyanate prepolymer consisting essentially of the reaction product of vinyl chloride and at least one other monomer capable of copolymerizing with vinyl chloride;
- where the thermoplastic copolymer contains at least 50% by weight vinyl chloride, at least 10% by weight of the monomer capable of copolymerizing with the vinyl chloride, and is free of isocyanate reactive groups.
A solvent free, moisture-curable, hot melt adhesive composition which is solid at room temperature, consisting essentially of a mixture of;
- a) from 60% to 95% by weight of an isocyanate terminated prepolymer with an isocyanate index greater than about 2.0, comprising the reaction product of;
- i. a polyisocyanate or mixture of polyisocyanates having an average functionality of from about 2.0 to about 2.3, and
- ii. an aliphatic polyester polyol or mixture of aliphatic polyester polyols;
- b) from 5% to 40% by weight of a thermoplastic copolymer that is compatible with the isocyanate prepolymer, having a weight average molecular weight greater than 30,000, consisting essentially of the reaction product of vinyl chloride and vinyl acetate where at least 50% by weight of the thermoplastic polymer is vinyl chloride and at least 10% by weight of the thermoplastic copolymer is vinyl acetate;
- c) up to 20% by weight a stabilizer selected from the group consisting of, epoxidized soybean oil, epoxidized tall oil, epoxy resin, epoxidized polybutadiene and mixtures thereof;
- d) optionally a catalyst;
- e) optionally a filler;
- f) optionally an antioxidant;
- g) optionally an adhesion promoter;
- h) optionally a tackifier;
- and
- i) optionally a wax
- where the percent by weight of each component is based on the total weight of the hot melt adhesive composition.
Dependencies are inferred from the claim text.