US 6,271,317 B1 · Asymmetrical tin-coupled rubbery polymers, and method of making

Abstract

Tire rubbers which are prepared by anionic polymerization are frequently coupled with a suitable coupling agent, such as a tin halide, to improve desired properties. It has been unexpectedly found that greatly improved properties for tire rubbers, such as lower hysteresis, can be attained by asymmetrically coupling the rubber. This invention more specifically discloses an asymmetrical tin-coupled rubbery polymer which is particularly valuable for use in manufacturing tire tread compounds, said asymmetrical tin-coupled rubbery polymer being comprised of a tin atom having at least three polydiene arms covalently bonded thereto, wherein at least one of said polydiene arms has a number average molecular weight of less than about 40,000, wherein at least one of said polydiene arms has a number average molecular weight of at least about 80,000, and wherein the ratio of the weight average molecular weight to the number average molecular weight of the asymmetrical tin-coupled rubbery polymer is within the range of about 2 to about 2.5.

Claims14

Dependent claims

A process for preparing an asymmetrical tin-coupled rubbery polymer which comprises:

(1) continuously polymerizing at least one diene monomer selected from the group consisting of 1,3-butadiene and isoprene to a conversion of at least about 90 percent utilizing an anionic initiator to produce a polymer cement containing living polydiene rubber wherein the living polydiene rubber chains are selected from the group consisting of isoprene-butadiene chains, isoprene chains, and butadiene chains, wherein some of the living polydiene rubber chains are low molecular weight polydiene rubber chains having a number average molecular weight of less than about 40,000, and wherein some of the living polydiene rubber chains are high molecular weight polydiene rubber chains having a number average molecular weight of greater than about 80,000;
and (2) continuously adding a tin halide to the polymer cement in a separate reaction vessel to produce the asymmetrically tin-coupled rubbery polymer, wherein said asymmetrical tin-coupled rubbery polymer has a polydispersity which is within the range of about 2 to about 2.5.

Dependencies are inferred from the claim text.

Asymmetrical tin-coupled rubbery polymers, and method of making