Sintering method
AssigneeSandvik AB
InventorsÅke Östlund, Leif Åkesson
Life of this patent
Estimating the term…
Abstract
There is disclosed a method of sintering cemented carbide bodies including heating said bodies to the sintering temperature in a suitable atmosphere and cooling. If said cooling at least to below 1200° C. is performed in a hydrogen atmosphere of pressure 0.4-0.9 bar cemented carbide bodies with no surface layer of binder phase are obtained. This is an advantage when said bodies are to be coated with wear resistant layers by the use of CVD-, MTCVD- or PVD-technique.
Claims8
A method of sintering cemented carbide bodies with a composition of 4 to 15 weight % Co, up to 20 weight % cubic carbides and rest WC comprising heating said bodies to sintering temperature and then cooling said bodies from the sintering temperature to a temperature of 1200° C. or below in a hydrogen atmosphere at a pressure of 0.4-0.9 bar.
A cemented carbide body having a nominal binder phase content comprising 5-10 weight % Co, WC, and an average WC grain size of 0.5-2 μm, the body comprising a 100-350 μm wide surface zone in which the average binder phase content in a 25 μm portion of the surface zone is 25-75% of the nominal binder phase content, the binder phase content in the surface zone increases monotonously and in a non-step-wise manner without maximum up to the nominal content, and the Co content on the surface of the body is +6/−4% of the nominal Co content of the entire body.
A method of producing a cemented carbide body, the cemented carbide body comprising hard constituents and a nominal binder phase content, the method comprising:
- providing the body with a composition wherein the hard constituents comprise WC, the binder phase comprises 4-15 weight % Co, and comprising up to 20 weight % cubic carbides;
- heating the body to sintering temperature;
- and
- cooling the body to a temperature of 1200° C. or below in a hydrogen atmosphere at a pressure of 0.4-0.9 bar thereby providing the body with a surface having a Co content approximately equal to the nominal Co content of the body.