Loading patent…
AssigneesDenso Corporation, Sumitomo Light Metal Industries, Ltd.
InventorsSunao Fukuda, Yoshihiko Kamiya, Taketoshi Toyama, Hirokazu Tanaka, Hiroshi Ikeda, Yoshifusa Shoji
Estimating the term…
An aluminum alloy clad material for heat exchangers exhibiting superior strength after brazing and excellent corrosion resistance is provided. The aluminum alloy clad material comprises a sacrificial anode material which is clad on one side of a core material, wherein the core material comprises an aluminum alloy comprising 0.3-2.0% of Mn, 0.25-1.0% of Cu, 0.3-1.1% of Si, and 0.05-0.35% of Ti with the remaining portion consisting of aluminum and impurities, the sacrificial anode material comprises an aluminum alloy comprising 1.5-8% of Zn, 0.01-0.8% of Si, and 0.01-0.3% of Fe with the remaining portion consisting of aluminum and impurities, and the total number of particles of Si compounds and Fe compounds with a particle diameter (circle equivalent diameter) of 1 μm or more present in the sacrificial anode material matrix is 2×104 or less per 1 mm2. The clad material is suitably used as a tube material or header plate material for automotive heat exchangers such as a radiator or heater core.
An aluminum alloy clad material for heat exchangers exhibiting high strength and excellent corrosion resistance comprising a sacrificial anode material which is clad on one side of a core material, wherein the core material comprises an aluminum alloy comprising 0.3-2.0% of Mn, 0.25-1.0% of Cu, 0.3-1.1% of Si, and 0.05-0.35% of Ti with the remaining portion consisting of aluminum and impurities, the sacrificial anode material comprises an aluminum alloy comprising 1.5-8% of Zn, 0.01-0.8% of Si, and 0.01-0.3% of Fe with the remaining portion consisting of aluminum and impurities, and the total number of particles of Si compounds and Fe compounds with a particle diameter (circle equivalent diameter) of 1 μm or more present in the sacrificial anode material matrix is 2×104 or less per 1 mm2.
An aluminum alloy clad material for heat exchangers exhibiting high strength and excellent corrosion resistance comprising a sacrificial anode material which is clad on one side of a core material and a brazing material of an Al—Si alloy which is clad on the other side of the core material, wherein the core material comprises an aluminum alloy comprising 0.3-2.0% of Mn, 0.25-1.0% of Cu, 0.3-1.1% of Si, and 0.05-0.35% of Ti with the remaining portion consisting of aluminum and impurities, the sacrificial anode material comprises an aluminum alloy comprising 1.5-8% of Zn, 0.01-0.8% of Si, and 0.01-0.3% of Fe with the remaining portion consisting of aluminum and impurities, and the total number of particles of Si compounds and Fe compounds with a particle diameter (circle equivalent diameter) of 1 μm or more present in the sacrificial anode material matrix is 2×104 or less per 1 mm2.
An aluminum alloy clad material for heat exchangers exhibiting high strength and excellent corrosion resistance comprising a sacrificial anode material which is clad on both sides of a core material, wherein the core material comprises an aluminum alloy comprising 0.3-2.0% of Mn, 0.25-1.0% of Cu, 0.3-1.1% of Si, and 0.05-0.35% of Ti with the remaining portion consisting of aluminum and impurities, the sacrificial anode material comprises an aluminum alloy comprising 1.5-8% of Zn, 0.01-0.8% of Si, and 0.01-0.3% of Fe with the remaining portion consisting of aluminum and impurities, and the total number of particles of Si compounds and Fe compounds with a particle diameter (circle equivalent diameter) of 1 μm or more present in the sacrificial anode material matrix is 2×104 or less per 1 mm2.
Dependencies are inferred from the claim text.