Reflective asphalt emulsions and method
OwnerJohn R. Fieldsinventor
Life of this patent
Estimating the term…
Abstract
A reflective asphalt emulsion is formed by dispersing asphalt into a slurry of colloidal clay at high shear and thereafter blending titanium dioxide and diatomaceous earth filler, and optionally acrylic latex, at low shear into the emulsion of clay and asphalt to form a white to light gray emulsion having a soft consistency and good shelf life. Particle sizes of the employed asphalt are controlled in order to preserve reflectivity of the finished emulsion.
Claims14
An asphaltic emulsion for coating a surface, said emulsion having a high reflectivity, the emulsion comprising bentonite clay, asphalt, and water, and produced by:
- preparing a slurry at a temperature of from 100° to 130° F. of bentonite clay and water with a dispersant;
- preheating an asphalt having a softening point of from about 100° to about 180° F. to a temperature within the range from about 240° to about 320° F.;
- and mixing said slurry with said asphalt while agitating at a shearing speed of about 2000 rpm to emulsify the slurry and asphalt into a paste;
- cooling said paste to below about 100° F.;
- blending at low shear, between about 1% and about 25% by weight titanium dioxide pigment, and a small quantity of diatomaceous earth filler into said paste so that the resulting paste has a white to light gray color and a soft consistency.
A reflective asphaltic emulsion comprising at least about 25% by weight asphalt, at least about 25% by weight water, an emulsifier, and between about 1% and about 25% by weight titanium dioxide pigment.
A reflective asphaltic emulsion comprising at least about 25% by weight asphalt, at least about 25% by weight water, an emulsifier, between about 1% and about 25% by weight titanium dioxide pigment, and a dispersant.
A reflective asphaltic emulsion comprising at least about 25% by weight asphalt, at least about 25% by weight water, an emulsifier, between about 1% and about 25% by weight titanium dioxide pigment, and a coagulant.
A reflective asphaltic emulsion comprising at least about 25% by weight asphalt, at least about 25% by weight water, an emulsifier, between about 1% and about 25% by weight titanium dioxide pigment, and acrylic latex pigment.
A reflective asphaltic emulsion comprising at least about 25% by weight asphalt, at least about 25% by weight water, an emulsifier, between about 1% and about 25% by weight titanium dioxide pigment, and about 1% rubber.
A reflective asphaltic emulsion comprising at least about 25% by weight asphalt, at least about 25% by weight water, an emulsifier, between about 1% and about 25% by weight titanium dioxide pigment, and a filler.
Dependencies are inferred from the claim text.