Propylene homopolymers and methods of making the same
AssigneeExxon Chemical Patents Inc.
InventorsChon-Yie Lin, Michael Chia-Chao Chen, Aspy Keki Mehta, Rajan K. Chudgar
Life of this patent
Estimating the term…
Abstract
This invention relates to isotactic propylene homopolymer compositions obtained from metallocene catalysis wherein the polymer has a molecular weight distribution (Mw/Mn) in the range of from about 2.5 to about 20.0. The isotactic propylene homopolymer composition may be prepared in a multiple stage polymerization process using the same metallocene component in at least two stages.
Claims11
A process for polymerizing isotactic polypropylene, said process comprising the steps of:
- (a) polymerizing propylene in the presence of a metallocene and a first concentration of chain transfer agent sufficient to produce a first propylene homopolymer having a melt flow rate in the range from 0.15 dg/min to 4.0 dg/min;
- (b) polymerizing propylene in the presence of the first propylene homopolymer in the presence of a second concentration of chain transfer agent sufficient to produce the isotactic polypropylene having a molecular weight distribution in the range of from about 2.5 to about 20.
A process for polymerizing isotactic polypropylene, said process comprising the steps of:
- (a) polymerizing propylene in the presence of a metallocene and a first concentration of chain transfer agent sufficient to produce a first propylene homopolymer having a melt flow rate in the range from 0.15 dg/min to 4.0 dg/min and a molecular weight distribution in the range of 1.8 to 2.5;
- (b) polymerizing propylene in the presence of the first propylene homopolymer in the presence of a second concentration of chain transfer agent sufficient to produce the isotactic polypropylene having a molecular weight distribution in the range of from about 2.5 to about 20.
A process for polymerizing isotactic polypropylene, said process comprising the steps of:
- (a) polymerizing propylene in a first reactor in the presence of a metallocene and a first concentration of chain transfer agent sufficient to produce a first propylene homopolymer having a melt flow rate in the range from 0.15 dg/min to 4.0 dg/min and a molecular weight distribution in the range of 1.8 to 2.5;
- (b) polymerizing propylene in a second reactor in the presence of the first propylene homopolymer in the presence of a second concentration of chain transfer agent sufficient to produce the isotactic polypropylene having a molecular weight distribution in the range of from about 2.5 to about 20.
A process for polymerizing isotactic polypropylene, said process comprising the steps of:
- (a) polymerizing propylene in the presence of a metallocene and a first concentration of chain transfer agent sufficient to produce a first propylene homopolymer having a melt flow rate in the range from 0.15 dg/min to 4.0 dg/min and a molecular weight distribution in the range of 1.8 to 2.5;
- (b) polymerizing propylene in the presence of the first propylene homopolymer in the presence of a second concentration of chain transfer agent sufficient to produce a second propylene homopolymer having a molecular weight distribution in the range of from about 1.8 to about 2.5.
A process for polymerizing isotactic polypropylene, said process comprising the steps of:
- (a) homopolymerizing propylene in the presence of a single metallocene and a first concentration of chain transfer agent sufficient to produce a first propylene homopolymer having a melt flow rate in the range from 0.15 dg/min to 4.0 dg/min and a molecular weight distribution in the range of 1.8 to 2.5;
- (b) homopolymerizing propylene in the presence of the first propylene homopolymer and the single metallocene in the presence of a second concentration of chain transfer agent sufficient to produce a second propylene homopolymer having a molecular weight distribution in the range of 1.8 to 2.5 and a melt flow rate in the range from 5 dg/min to 1000 dg wherein the isotactic polypropylene is a blend of the first and second homopolymer having a molecular weight distribution in the range of from about 2.5 to about 20 and wherein the first homopolymer comprises from 40 percent to 80 percent of the isotactic polypropylene and the second homopolymer comprises from 20 percent to 60 percent of the isotactic polypropylene.
Dependencies are inferred from the claim text.