Compacts based on pyrogenically produced silicon dioxide

Abstract

Compacts based on pyrogenically produced silicon dioxide and having the following physical and chemical characteristics: Outer diameter 0.8-20 mm BET surface area 30-400 m2/g Pore volume 0.5-1.3 ml/g Breaking strength 10-250N Composition >99.8 wt. % SiO2 Other constituents <0.2 wt. % Abrasion <5 wt. % Apparent weight 350-750 g/l are produced in that pyrogenically produced silicon dioxide is homogenized with methyl cellulose, microwax and polyethylene glycol with addition of water, dried at a temperature of 80-150° C. and comminuted to a powder, optionally the powder is compressed into compacts, and heat-treated at a temperature of 400 to 1200° C. for a time of 0.5 to 8 hours. These compacts can be used as catalysts or catalyst carriers in vinyl acetate monomer production and ethylene hydration.