Metal nitrides as performance modifiers for glass compositions
AssigneeLibben-Owens-Ford Co.
InventorsSrikanth Varanasi, Paige L. Higby, Gwendolyn A. Young
Life of this patent
Estimating the term…
Abstract
Silicate based glass compositions with nitrogen compounds are included in the composition as performance modifiers to impart desirable color and improved energy absorbance properties. The nitrogen compound is, generally, a metal nitride which is added to the batch glass composition in amounts greater than 0.05 weight percent prior to melting the composition and method resulting in a finished glass suitable for use in architectural and automotive glazings.
Claims6
A glazing produced by the admixing, heating and melting of a batch glass composition comprising:
- a) a soda-lime-silica float glass batch mixture including from about 65 to about 80 weight percent SiO2 from about 10 to about 20 weight percent Na2O, from about 5 to about 15 weight percent CaO, from about 0 to about 10 MgO, from about 0 to about 5 weight percent Al2O3, from about 0 to about 5 weight percent K2O, from about 0 to about 5 weight percent BaO, from about 0 to about 5 weight percent B2O3, from about 0 to about 5 weight percent Ga2O3;
- b) an amount of at least one metal nitride;
- and
- c) an amount of an iron-containing compound or compounds so as to result in a finished glass having a total iron content, measured as Fe2O3, of about 0.1 to about 4.5 weight percent, wherein said glazing has an Illuminant A visible light transmittance of greater than 70% and a direct solar heat transmittance of less than 44% at a nominal thickness of 3-6 mm.
An automotive glazing unit, comprising two sheets of a soda-lime-silica glass integrally adhered together through an interposed layer of transparent resinous material, said glass including an amount of nitrogen, such nitrogen resulting from the admixing, melting, and heating of at least one metal nitride in a batch glass composition.
Dependencies are inferred from the claim text.