Ideal oxygen precipitating silicon wafers and oxygen out-diffusion-less process therefor

A process for heat-treating a single crystal silicon wafer sliced from a single crystal silicon ingot grown by the Czochralski method to influence the precipitation behavior of oxygen in the wafer in a subsequent thermal processing step, the silicon wafer having a front surface, a back surface, a central plane between the front and back surfaces, a front surface layer which comprises the region of the wafer between the front surface and a distance, D, measured from the front surface and toward the central plane, and a bulk layer which comprises the region of the wafer between the central plane and front surface layer, the process comprising the steps of:

• subjecting the wafer to a heat-treatment to form crystal lattice vacancies in the front surface and bulk layers, and
• controlling the cooling rate of the heat-treated wafer to produce a wafer having a vacancy concentration profile in which the peak density is at or near the central plane with the concentration generally decreasing in the direction of the front surface of the wafer and the difference in the concentration of vacancies in the front surface and bulk layers being such that a thermal treatment at a temperature in excess of 750° C., is capable of forming in the wafer a denuded zone in the front surface layer and oxygen clusters or precipitates in the bulk zone with the concentration of the oxygen clusters or precipitates in the bulk layer being primarily dependant upon the concentration of vacancies.