Nickel hydroxide active material for use in alkaline storage cell and manufacturing method of the same
AssigneeSanyo Electric Co., Ltd.
InventorsYoshitaka Baba, Motoo Tadokoro, Takayuki Yano
Life of this patent
Estimating the term…
Abstract
A nickel hydroxide active material for use in an alkaline storage cell, the active material being essentially composed of nickel hydroxide particles covered with a cobalt compound adhered to their surfaces, wherein the cobalt compound is disordered in a crystal structure and formed in a higher order state containing alkali cation, and wherein the nickel hydroxide is in the form of a higher order nickel compound having an average oxidation value of 2.15 to 2.40.
Claims6
A nickel hydroxide active material for use in an alkaline storage cell, the active material being essentially composed of nickel hydroxide particles covered with a cobalt compound adhered to their surfaces, wherein the cobalt compound has a disordered crystal structure and is formed on the surfaces of the nickel hydroxide particles in an average oxidation value of more than 2 and contains alkali cation, and wherein the nickel hydroxide particles are in the form of a higher order nickel compound having an average oxidation value of 2.15 to 2.40.
A method of manufacturing a nickel hydroxide active material for use in an alkaline storage cell, said method comprising the steps of:
- (a) adhering a cobalt compound of equal to or less than 2 in average oxidation value to nickel hydroxide particles;
- (b) subjecting the cobalt compound adhered to the nickel hydroxide particles to heat treatment in the presence of an alkaline solution and oxygen so that the cobalt compound formed on the nickel hydroxide particles is disordered in crystal structure and contains alkali cations;
- (c) mixing the prepared nickel hydroxide particles subjected to heat treatment in step (b) with an alkaline solution to produce a slurry;
- and
- (d) charging an active material essentially composed of the treated nickel hydroxide particles in such a manner that the slurry is electrochemically oxidized to convert the treated nickel hydroxide particles to a higher order nickel compound having an average oxidation value of 2.15 to 2.40.
Dependencies are inferred from the claim text.