US 6,191,210 B1Granted

Water-dilutable binders, aqueous paints containing these binders, and process for priming or painting plastics materials with a single coat of paint

AssigneeBASF Coatings GmbH

InventorsJoachim Rösch, Harald Borgholte, Horst Hintze-Brüning

Life of this patent

Estimating the term…

Loading patent…

Abstract

The invention relates to water-dilutable binders which can be prepared by subjecting (A) from 20 to 90% by weight of a mixture of (a1) from 3 to 50% by weight of acrylic acid, methacrylic acid or of a mixture of acrylic acid and methacrylic acid, and (a2) from 50 to 97% by weight of an ethylenically unsaturated monomer or of a mixture of ethylenically unsaturated monomers to free-radical polymerization in the presence of (B) from 9.9 to 79.9% by weight of a halogen-free copolymer composed of (b1) from 1 to 99, preferably from 50 to 90% by weight, of propylene, (b2) from 1 to 99, preferably from 10 to 50% by weight, of at least one olefin which is copolymerizable with (b1) and contains per molecule from five to twenty, preferably from six to eight, carbon atoms, with the exception of isoprene, and (b3) from 0 to 50, preferably from 0 to 25% by weight, of ethylene and/or butylene, or of a mixture of such copolymers, and (C) from 0.1 to 10% by weight of a free-radical initiator or of a mixture of free-radical initiators, and, after neutralization of at least 20% of the carboxyl groups which are present in the resulting polymerization product, dispersing the polymerization product in water, the sum of the percentages by weight of components (A), (B) and (C) and of (a1) and (a2) being in each case always 100% by weight, and the composition of the mixture of (al) and (a2) being selected such that polymerization of the mixture of (al) and (a2) alone gives a polymer which has a glass transition temperature of from 0 to 150° C., and contains from 0.04 to 1.0 milliequivalent of one or more of the following functional groups: —COOH, —OH, —NR3, —CN, —CONH2, —CO—, —NHCONH—, —OCONH—, —OP3H, —OSO3H, —R—O—R—, where R is an organic radical.

Claims10

Dependent claims

An aqueous coating material, comprising at least one water-dilutable binder resulting from the free-radical polymerization of:

(A) from 20 to 90% by weight of a mixture of monomers, comprising:
(a1) from 3 to 50% by weight of a first monomer selected from the group consisting of acrylic acid, methacrylic acid and mixtures thereof, and
(a2) from 50 to 97% by weight of an ethylenically unsaturated second monomer which is different from said first monomer (a1) or a mixture of such ethylenically unsaturated monomers,
wherein the composition of said mixture of monomers (a1) and (a2) is selected such that polymerization of said mixture of monomers (a1) and (a2) alone gives a polymer which
has a glass transition temperature of from 0 to 150 degrees C.,
contains from 0.04 to 1.0 milliequivalents of one or more of the following functional groups:
—COOH, —OH, —NR3, —CN, —CONH2, —CO—, —NHCONH—, —OCONH—, —OPO3H, —OSO3H, —R—OR—R—, (where R is an organic radical), and
comprises from 0 to 50% by weight of one or more cycloaliphatic groups substituted by at least one alkyl group having 1 to 12 carbon atoms and selected from the group consisting of cyclopentyl, cyclohexyl, perhydronapthyl, perhydroanthracyl, perhydrophenanthryl, adamantyl, isobornyl, bicyclohexyl, bicycloheptyl, bicyclooctyl, bicyclononyl, bicyclodecyl, bicycloundecyl, biciclododecyl groups and mixtures thereof;
in the presence of
(B) from 9.9 to 79.9% by weight of a halogen-free copolymer composed of:
(b1) from 1 to 99% of propylene;
(b2) from 1 to 99% by weight of at least one olefin which is copolymerizable with (b1) and which contains per molecule from five to twenty carbon atoms, with the exception of isoprene, and
(b3) from 0 to 50% by weight, of a member of the group consisting of ethylene butylene, and mixtures thereof,
or of a mixture of such copolymers, and
(C) from 0.1 to 10% by weight of a free-radical initiator or a mixture of free-radical initiators,
and, after neutralization of at least 20% of the carboxyl groups which are present in the resulting polymerization product,
dispersing the polymerization product in water,
wherein the sum of the percentages by weight of components (A), (B), and (C) and of (a1) and (a2) and (b1), (b2) and (b3) is, in each case, always 100% by weight.

15 more elements

An aqueous coating composition, comprising

from 30 to 80 percent by weight of water,
from 6 to 70 percent by weight of a water-dilutable binder, the percentages by weight being based on the overall formulation of the aqueous coating composition and said binder comprising
the reaction product of the free-radical polymerization of:
(A) from 20 to 90% by weight of a mixture of
(a1) from 3 to 50% by weight of a monomer selected from the group consisting of acrylic acid, methacrylic acid and mixtures thereof, and
(a2) from 50 to 97% by weight of an ethylenically unsaturated monomer which is different from (a1) or a mixture of such ethylenically unsaturated monomers,
in the presence of
(B) from 9.9 to 79.9% by weight of a halogen-free copolymer composed of
(b1) from 1 to 99% of propylene,
(b2) from 1 to 99% by weight of at least one olefin which is copolymerizable with (b1) and contains per molecule from five to twenty, preferably from six to eight, carbon atoms, with the exception of isoprene, and
(b3) from 0 to 50% by weight, of a member of the group consisting of ethylene, butylene, and mixtures thereof,
or of a mixture of such copolymers, and
(C) from 0.1 to 10% by weight of a free-radical initiator or of a mixture of free-radical initiators,
wherein
at least 20% of the carboxyl groups which are present in the resulting polymerization product are neutralized and the polymerization product is dispersed in water to provide a substantially homogenous mixture,
the sum of the percentages by weight of components (A), (B) and (C) and of (a1) and (a2) and (b1), (b2) and (b3) are based on the total weight of the aqueous composition, and
the composition of the mixture of (a1) and (a2) is selected such that polymerization of the mixture of (a1) and (a2) alone gives a polymer which
has a glass transition temperature of from 0 to 150° C.,
contains from 0.04 to 1.0 milliequivalent of one or more of the following functional groups:
—COOH, —OH, —NR3, —CN, —CONH2, —CO—, —NHCONH—, —OCONH—, OPO3H, —OSO3H, —R—O—R—, (where R is an organic radical), and
comprises from 0 to 50% by weight of one or more cycloaliphatic groups substituted by at least one alkyl group having 1 to 12 carbon atoms and selected from the group consisting of cyclopentyl, cyclohexyl, perhydronaphtyl, perhydroanthracyl, perhydrophenanthryl, adamantyl, isobornyl, bicyclohexyl, bicycloheptyl, bicyclooctyl, bicyclononyl, bicyclodecyl, bicycloundecyl, bicyclododecyl groups and mixtures thereof, and
the water and the water-dilutable binder being mixed so as to provide a substantially homogenous and stable mixture.

19 more elements